Abstract:Digital light processing (DLP) 3D-printed Si3N4 ceramics, known for their exceptional performance, offer distinct advantages in meeting the high-strength and complex structural demands of industries such as aerospace, semiconductors, healthcare, automotive, energy, and machinery. However, due to Si3N4's strong chemical stability, low diffusion rate, low self-sintering ability, and high melting point, achieving densification under conventional sintering conditions is challenging. As a result, sintering additives are essential to promote the sintering process, lower the sintering temperature, improve densification, and enhance performance. In this study, 45 vol% Si3N4 slurries were prepared using DLP 3D printing technology, incorporating nine different combinations of sintering additives, including aluminum oxide (Al2O3), yttrium oxide (Y2O3), and aluminum nitride (AlN), in various ratios with Si3N4. The slurries were then sintered at 1800 °C for 2 h under a 1 MPa N2 atmosphere. Additionally, the phase composition, microstructure, grain distribution, and crack propagation of the materials. The results showed that a Si3N4 to Al2O3 and Y2O3 ratio of 95:2.5:2.5 produced elongated β-Si3N4 grain structures and enhanced density, achieving a maximum Vickers hardness of 12.88 ± 0.52 GPa. Additionally, the synergistic toughening effect of the rod-like β-Si3N4 grains and sintering aids significantly improved the fracture toughness of the Si3N4 ceramic matrix, with a flexural strength of 540.63 ± 10.05 MPa and a fracture toughness of 4.92 ± 0.07 MPa·m1/2. This study lays the foundation for the future application of 3D-printed Si3N4 ceramics, optimization of sintering aid combinations at different ratios, and performance enhancement in extreme environments.

Effects of different types of sintering additives and post-heat treatment (PHT) on the mechanical properties of SHS-fabricated Si3N4 ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Effects of Sintering Additive and Β-Si3n4 Phase Contents on the Properties of Porous Si3N4 Ceramics

Fabrication of Si3N4 Ceramics with High Thermal Conductivity and Flexural Strength Via Novel Two-Step Gas-Pressure Sintering

Effect of Sintering Additives on Microstructure and Mechanical Properties of Porous Silicon Nitride Ceramics

Effects of MgSiN2 Addition and Post-Annealing on Mechanical and Thermal Properties of Si3N4 Ceramics

Silicon Nitride Ceramics with High Thermal Conductivity and Excellent Mechanical Properties Fabricated with MgF2 Sintering Aid and Post Sintering Heat Treatment

Effects of sintering additives on mechanical properties and microstructure of Si3N4 ceramics by microwave sintering

Fabrication of Si 3 N 4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Effect of Post-Sintering Heat-Treatment on Thermal Conductivity of Si3N4 Ceramics Containing Different Additives

Effect of MgF2 addition on mechanical properties and thermal conductivity of silicon nitride ceramics

Effects of Sintering Additives on Properties of Porous Silicon Nitride Ceramics Fabricated by Carbothermal Reduction

Influence of sintering additives on densification kinetics and high-temperature strength in γ-Y2Si2O7 ceramics

Impact of Sintering Aid Type and Content on the Mechanical Properties of Digital Light Processing 3D-Printed Si3N4 Ceramics

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Effect of Composite Sintering Additives Containing Non-Oxide on Mechanical, Thermal and Dielectric Properties of Silicon Nitride Ceramics Substrate

Effects of α-Si3N4 seeds and sintering additives on properties of porous silicon nitride ceramics fabricated by carbothermal reduction