Abstract:This paper introduces an approach to preparing high‐strength Si3N4 ceramics using vat photopolymerization with a bi‐phase particle size gradation strategy. The influence of different ratios of coarse β‐Si3N4 powders (Cβ) and fine α‐Si3N4 powders (Fα) on the slurry performance, microstructure evolution, and final ceramic strength was systematically studied. It was found that an appropriate particle size gradation can significantly reduce the viscosity of the slurry. The curing depth of Si3N4 slurries decreases with increasing Fα content, while the stability increases. During sintering, dissolved Fα‐Si3N4 not only directly precipitates into small elongated β‐Si3N4 grains but also onto the neighboring Cβ‐Si3N4, promoting the development of large elongated β‐Si3N4 grains and resulting in a bimodal microstructure distribution. The highest strength of Si3N4 ceramics was achieved with a ratio of 6:4 Cβ to Fα Si3N4 powders. Under these conditions, the Si3N4 ceramics exhibited a flexural strength of 472 MPa, significantly higher than that of Si3N4 ceramics prepared using pure Cβ/Fα powders. The strength improvement is primarily due to the well‐designed bi‐phase particle size gradation strategy, which optimizes slurry performance, minimizes defects that may be introduced during the green part printing process while controlling the microstructure evolution during sintering, achieves the ideal bimodal microstructure distribution. The outcomes of this research demonstrate the feasibility of using vat photopolymerization with bi‐phase particle size gradation for the preparation of high‐strength Si3N4 ceramics, which has great potential for application in the manufacturing of various ceramic products.

Preparation of Si3n4 Ceramics with High Strength and High Reliability Via A Processing Strategy

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

PREPARING Si3N4 CERAMICS WITH HIGH PERFORMANCE BY GELCASTING (II)-INFLUENCE OF CIP, POWDER OXIDIZATION AND GPS SCHEME ON PROPERTIES OF THE MATERIALS

PREPARING Si3N4 CERAMICS WITH HIGH PERFORMANCES BY GELCASTING (I)INFLUENCE OF COATING Si3N4 POWDER ON MECHANICAL PROPERTIES OF THE MATERIAL

Microstructure and Properties of Si3N4 Based on Gelcasting

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Preparation of high‐strength Si3N4 ceramics via vat photopolymerization: A bi‐phase particle size gradation strategy

A new approach for the net-shape fabrication of porous Si3N4 bonded SiC ceramics with high strength

Preparation and study of porous Si3N4 ceramics with high strength

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Fused Deposition Modeling of Si3N4 Ceramics: A Cost-Effective 3D-Printing Route for Dense and High Performance Non-Oxide Ceramic Materials

Preparation of in-situ synthesized SiC particles reinforced highly porous Si3N4 ceramics by gel-casting

Silicon Nitride Ceramics Consolidated by Oscillatory Pressure Sintering

Preparation of <i>In Situ</i> Synthesized SiC Particles Reinforced Highly Porous Si<sub>3</sub>N<sub>4</sub> Ceramics by Gel-Casting

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Fabrication, Structure and Properties of Porous SiC Ceramics with High Porosity and High Strength

Microstructure and Mechanical Properties of Three Porous Si3n4 Ceramics Fabricated by Different Techniques

Fabrication of Si3N4 Ceramics with High Thermal Conductivity and Flexural Strength Via Novel Two-Step Gas-Pressure Sintering

Influence of fabricated process on mechanical properties of porous SiC-particle/ Si3N4 composites

Defects control of silicon nitride ceramics by oscillatory pressure sintering and consequent hot isotropic pressing