Abstract:Porous Si3N4 ceramics with bimodal hierarchical pore structures were fabricated through combining aqueous gelcasting and adding pore–forming agent method wherein a low–toxic monomer N, N–dimethylacrylamide (DMAA) and spherical pore–forming agent polystyrene sphere (PS) were respectively applied. The results demonstrated that PS size and content played an important function in regulating microstructure and properties of slurries, green and sintered bodies. The slurry viscosity increased sharply with the introduction of fine PS and reached a maximum of 1.78 Pa⋅s when adopting 7 wt% PS with d50 = 2.51 μm. Fine PS addition caused higher porosity in green bodies than coarse one, resulting in a significant reduction in bending strength from 28.50 MPa to 11.50 MPa, however, overall, demonstrating high enough strength for mechanical processing. The formed spherical pores from PS in ceramic matrix facilitated high porosity and highly crosslinked microstructure, thus contributing to lowering dielectric constant and loss. With PS size increasing, the dominant role in mechanical properties was transferred from porosity to microstructure, whilst dielectric properties were merely controlled by porosity and spherical pores. The porosity, bending strength, fracture toughness, dielectric constant and loss at 15 GHz varied in ranges of 36.34–52.91%, 258.42–101.21 MPa, 6.02–3.38 MPa⋅m1/2, 4.29–2.98 and 1.48–1.18 × 10−3, respectively, displaying an excellent comprehensive properties.

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Porous Si3N4-based Ceramics with Uniform Pore Structure Originated from Single-Shell Hollow Microspheres

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

In-situ Reaction Synthesis of Porous Si2N2O-Si3N4 Multiphase Ceramics with Low Dielectric Constant Via Silica Poly-Hollow Microspheres

Porous Si3N4 ceramics with hierarchical pore structures prepared by gelcasting using DMAA as gelling agent and PS as pore–forming agent

Porous Silica Ceramics with Uniform Pores from the In-Situ Foaming Process of Silica Poly-Hollow Microspheres in Inert Atmosphere

3D printing of porous SiC ceramics added with SiO2 hollow microspheres

Fabrication, Structure and Properties of Porous SiC Ceramics with High Porosity and High Strength

Preparation of porous Si 3 N 4 ceramics via tailoring solid loading of Si 3 N 4 slurry and Si 3 N 4 poly-hollow microsphere content

A Novel Method of Strong and Tough Si3N4 Ceramic from the Particle‐stabilized Foam

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

A New Al 2 O 3 Porous Ceramic Prepared by Addition of Hollow Spheres

Ultrahigh-Strength Porous Ceramic Composites via a Simple Directional Solidification Process

A non-sintering fabrication method for porous Si3N4 ceramics via sol hydrothermal process

Pore Morphology Designs of Porous Si3n4-Based Ceramics Using Si3n4 and Al2o3 Poly-Hollow Microspheres As Pore-Forming Agents

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres