Abstract:Porous ceramic microspheres have been widely used in many fields such as drug delivery, chemical catalysis, environmental protection, noise reduction by absorption, and separation and purification. However, the methodology to prepare porous ceramic microspheres based on traditional colloidal processing routes faces the problems of precise control of the diameter, degree of sphericity, uniformity of the microstructure (size, porosity, shape, etc.), and so forth. Herein, we propose a new methodology to prepare hierarchically porous ceramic microspheres with a mechanism based on the superwettability strategy without the requirement of any special equipment or complicated procedures. In such an approach, a ceramic emulsion with an extremely low viscosity was prepared by an emulsion-assisted self-assembly method, which would be repelled on the superamphiphobic surface to form a submillimeter-sized Al2O3 microsphere. Compared with the traditional colloidal processing approaches to prepare ceramic microspheres, the homogeneity and precision of the ceramic microspheres prepared via our approach are much finer, while our approach is quite simple, highly efficient, and cost-saving. Moreover, the diameter of the microspheres and the microstructure of the pores (size, density, porosity, etc.) in the ceramic microspheres could be flexibly manipulated. Our methodology has solved the key problems in the preparation of ceramic microspheres which have not been solved in the past decades and provided the solution for engineering through the delicate scientific design. We anticipate that this example of the combination of superwettability science with traditional structural ceramics could provide an important application direction of advanced techniques for fabricating ceramics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c05324?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c05324</a>.Contact angle, laser scanning confocal microscopy images, surface roughness Ra and Rq, optical microscopy image, mean pore size, density of the pore, and SEM images of the Si3N4 ceramic microspheres (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c05324/suppl_file/am0c05324_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Porous Si3N4-based Ceramics with Uniform Pore Structure Originated from Single-Shell Hollow Microspheres

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

In-situ Reaction Synthesis of Porous Si2N2O-Si3N4 Multiphase Ceramics with Low Dielectric Constant Via Silica Poly-Hollow Microspheres

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Porous Silica Ceramics with Uniform Pores from the In-Situ Foaming Process of Silica Poly-Hollow Microspheres in Inert Atmosphere

Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres

Porous Si3N4 ceramics with hierarchical pore structures prepared by gelcasting using DMAA as gelling agent and PS as pore–forming agent

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

3D printing of porous SiC ceramics added with SiO2 hollow microspheres

Preparation, mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by a New Water-Based Freeze Casting

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Pore Structure Control of Si3n4 Ceramics Based on Particle-Stabilized Foams

Pore Morphology Designs of Porous Si3n4-Based Ceramics Using Si3n4 and Al2o3 Poly-Hollow Microspheres As Pore-Forming Agents

Preparation and Performance of Si3N4 Hollow Microspheres by the Template Method and Carbothermal Reduction Nitridation

Preparation of porous Si 3 N 4 ceramics via tailoring solid loading of Si 3 N 4 slurry and Si 3 N 4 poly-hollow microsphere content

Fabrication and properties of Si2N2O-Si3N4 ceramics via direct ink writing and low-temperature sintering

Novel Strategy To Prepare Hierarchically Porous Ceramic Microspheres via a Self-Assembly Method on Tunable Superamphiphobic Surfaces

Fabrication and Properties of Porous Mullite Ceramics from Directly Sintering Ceramic Microspheres

Porous SiC Ceramics with Controllable Porosity Achieved by Micro-sized Powder through Recrystallization Sintering