Abstract:The porous SiC–Si3N4 composite ceramics with good EMW absorption properties were prepared by combination of gelcasting and carbothermal reduction. The pre-oxidation of Si3N4 powders significantly improved the rheological properties of slurries (0.06 Pa s at 103.92 s−1) and also suppressed the generation of NH3 and N2 from Si3N4 hydrolysis and reaction between Si3N4 and initiator APS, thereby reducing the pore defects in green bodies and enhancing mechanical properties with a maximum value of 42.88 MPa. With the extension of oxidation time from 0 h to 10 h, the porosity and pore size of porous SiC–Si3N4 composite ceramics increased from approximately 41.86% and 1.0–1.5 μm to 46.33% and ~200 μm due to the production of CO, N2 and gaseous SiO, while the sintering shrinkage decreased from 16.24% to 10.50%. With oxidation time of 2 h, the Si2N2O fibers formed in situ by the reaction of Si3N4 and amorphous SiO2 effectively enhanced the mechanical properties, achieving the highest flexural strength of 129.37 MPa and fracture toughness of 4.25 MPa m1/2. Compared with monolithic Si3N4 ceramics, the electrical conductivity, relative permittivity and dielectric loss were significantly improved by the in-situ introduced PyC from the pyrolysis of three-dimensional network DMAA-MBAM gel in green bodies and the SiC from the carbothermal reduction reaction between PyC and SiO2 and Si3N4. The porous SiC–Si3N4 composite ceramics prepared by the unoxidized Si3N4 powders demonstrated the optimal EMW absorption properties with reflection loss of −22.35 dB at 8.37 GHz and 2 mm thickness, corresponding to the effective bandwidth of 8.20–9.29 GHz, displaying great application potential in EMW absorption fields.

Preparation, mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics

Porous SiC-Si2N2O-Si3N4 composite ceramics with excellent EMW absorption properties prepared by gelcasting and carbonthermal reduction

Construction of Si<sub>3</sub>N<sub>4</sub>/SiO<sub>2</sub>/SiC-Y<sub>2</sub>Si<sub>2</s ub>O<sub>7</sub> composite ceramics with gradual impedance matching structure for high-temperature electromagnetic wave absorption

Porous SiC–Si3N4 composite ceramics with excellent EMW absorption property prepared by gelcasting using DMAA

Nano-SiC-decorated Y2Si2O7 Ceramic for Enhancing Electromagnetic Waves Absorption Performance

Dielectric and Microwave Absorption Properties of SiCnw-SiBCN Composite Ceramics Deposited Via Chemical Vapor Infiltration

Significantly toughened SiC foams with enhanced microwave absorption via in situ growth of Si3N4 nanowires

Enhanced electromagnetic wave absorption properties of a novel SiC nanowires reinforced SiO2/3Al2O3·2SiO2 porous ceramic

Dielectric and microwave-absorption properties of SiC nanoparticle/SiBCN composite ceramics

Simultaneously Enhancing Mechanical and Microwave Absorption Properties of Cf/SiC Composites Via SiC Nanowires Additions

Multiscale SiCnw and carbon fiber reinforced SiOC ceramic with enhanced mechanical and microwave absorption properties

Tuning SiC nanowires interphase to improve the mechanical and electromagnetic wave absorption properties of SiCf/SiCnw/Si3N4 composites

Improved Electromagnetic Absorbing Properties of Si3N4–SiC/SiO2 Composite Ceramics with Multi-Shell Microstructure

In Situ Growth of One-Dimensional Nanowires on Porous PDC-SiC/Si3N4 Ceramics with Excellent Microwave Absorption Properties

Synthesis and tunable electromagnetic shielding and absorption performance of the three-dimensional SiC nanowires/carbon fiber composites

Dielectric Property of Si<sub>3</sub>N<sub>4</sub>/SiBCN Composite Ceramics Doped with SiC

Mechanical and Microwave-Absorption Properties of Si3N4 Ceramic with SiCNFs Fillers

Increased microwave absorption property of porous Si3N4 ceramics by loading polymer-derived SiCN for a multifunctional design

Electromagnetic Properties of Porous Si3N4 Ceramics with Gradient Distributions of SiC and Pores Fabricated by Directional In–situ Nitridation Reaction

Multifunction properties of SiOC reinforced with carbon fiber and in-situ SiC nanowires

Effect of an annealing treatment on the microstructure and EMW-absorbing properties of SiCw/Si3N4 ceramics fabricated by 3D printing