Effect of an annealing treatment on the microstructure and EMW-absorbing properties of SiCw/Si3N4 ceramics fabricated by 3D printing

Siwen Yu,Tao Zeng,Yipeng Yang,Honghao Jiang,Rina Wu,Meiling Fan,Su Cheng

DOI: https://doi.org/10.1016/j.ceramint.2022.09.084

IF: 5.532

2023-01-01

Ceramics International

Abstract:SiC whisker (SiCw)/Si3N4 ceramics were prepared via selective laser sintering (SLS) and precursor infiltration pyrolysis (PIP) to achieve good electromagnetic wave (EMW) absorption performance. The as-pyrolyzed composite ceramics were annealed at 1200–1600 °C in a N2 atmosphere. The microstructural variation, phase evolution, and EMW-absorbing properties of the SiCw/Si3N4 ceramics were subsequently studied. SiC whiskers were generated in the composite ceramics during pyrolysis, and their content increased as a function of the annealing temperature. An increase in the SiCw content of the annealed samples improved the reflection loss of the composite ceramics. The absorption properties of the SiCw/Si3N4 ceramics first degraded and then improved with increasing annealing temperature. Among all the samples tested, the composite ceramics annealed at 1600 °C showed the optimal EMW absorption performance in the range of 2–18 GHz due to the lower content of free carbon and higher content of SiCw. The ceramics annealed at 1600 °C exhibited a superior absorption loss of −14.1 dB and an effective absorption bandwidth of 2.16 GHz. These results demonstrate that the EMW-absorbing performance of the SiCw/Si3N4 ceramics was significantly improved after annealing at 1600 °C. Thus, SiCw/Si3N4 composite parts with complex shapes were successfully manufactured by combining the SLS and PIP processes.

materials science, ceramics