Preparation and electromagnetic wave absorption properties of PDC–SiC/Si 3 N 4 composites using selective laser sintering and infiltration technology

Siwen Yu,Tao Zeng,Jue Zhao,Honghao Jiang,Zuzheng Chen,Yipeng Yang,Zhiqiang Zhong,Su Cheng

DOI: https://doi.org/10.1016/j.jmrt.2023.01.202

IF: 6.267

2023-02-16

Journal of Materials Research and Technology

Abstract:Polymer-derived silicon carbide/silicon nitride (PDC–SiC/Si 3 N 4 ) composites were prepared by additive manufacturing and infiltration technology. The composite green bodies were prepared using selective laser sintering (SLS) three-dimensional (3D) printing technology. Carbon-rich PDC–SiC was generated via precursor infiltration and pyrolysis (PIP) to increase the dielectric constant and enhance the electromagnetic wave (EMW) attenuation ability of the composites. Low-dielectric materials, including Al 2 O 3 , TiO 2 , and AlPO 4 , were introduced by sol infiltration to improve the impedance-matching characteristics of the composites. The results showed that the EMW absorption ability of the PDC–SiC/Si 3 N 4 composites enhanced after two and four PIP cycles, whereas it degraded with further increasing the PIP cycle number. Among all the samples, the PDC–SiC/Si 3 N 4 composite after four PIP cycles displayed an excellent EMW absorption ability with the minimal reflection loss of −46.79 dB, whereas its effective absorption bandwidth was narrow. Comparing to the sample without infiltration, the effective absorption bandwidth of the samples after the infiltration treatment with TiO 2 or Al(H 2 PO 4 ) 3 sol increased from 1.44 GHz to 4.08 GHz and 3.52 GHz, respectively. These results demonstrate that the PIP process and infiltration with TiO 2 or Al(H 2 PO 4 ) 3 sol resulted in a 3D-printed PDC–SiC/Si 3 N 4 ceramic that is a promising EMW absorption material suitable for high-temperature environments.

materials science, multidisciplinary,metallurgy & metallurgical engineering