Abstract:Digital light processing (DLP) 3D-printed Si3N4 ceramics, known for their exceptional performance, offer distinct advantages in meeting the high-strength and complex structural demands of industries such as aerospace, semiconductors, healthcare, automotive, energy, and machinery. However, due to Si3N4's strong chemical stability, low diffusion rate, low self-sintering ability, and high melting point, achieving densification under conventional sintering conditions is challenging. As a result, sintering additives are essential to promote the sintering process, lower the sintering temperature, improve densification, and enhance performance. In this study, 45 vol% Si3N4 slurries were prepared using DLP 3D printing technology, incorporating nine different combinations of sintering additives, including aluminum oxide (Al2O3), yttrium oxide (Y2O3), and aluminum nitride (AlN), in various ratios with Si3N4. The slurries were then sintered at 1800 °C for 2 h under a 1 MPa N2 atmosphere. Additionally, the phase composition, microstructure, grain distribution, and crack propagation of the materials. The results showed that a Si3N4 to Al2O3 and Y2O3 ratio of 95:2.5:2.5 produced elongated β-Si3N4 grain structures and enhanced density, achieving a maximum Vickers hardness of 12.88 ± 0.52 GPa. Additionally, the synergistic toughening effect of the rod-like β-Si3N4 grains and sintering aids significantly improved the fracture toughness of the Si3N4 ceramic matrix, with a flexural strength of 540.63 ± 10.05 MPa and a fracture toughness of 4.92 ± 0.07 MPa·m1/2. This study lays the foundation for the future application of 3D-printed Si3N4 ceramics, optimization of sintering aid combinations at different ratios, and performance enhancement in extreme environments.

Fused Deposition Modeling of Si3N4 Ceramics: A Cost-Effective 3D-Printing Route for Dense and High Performance Non-Oxide Ceramic Materials

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Impact of Sintering Aid Type and Content on the Mechanical Properties of Digital Light Processing 3D-Printed Si3N4 Ceramics

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Mechanical and dielectric properties of Si3N4-SiO2 ceramics prepared by digital light processing based 3D printing and oxidation sintering

Fabrication of Si3N4–SiC/SiO2 composites using 3D printing and infiltration processing

Preparation of Si3n4 Ceramics with High Strength and High Reliability Via A Processing Strategy

Additive manufacturing of complexly shaped SiC with high density via extrusion-based technique – Effects of slurry thixotropic behavior and 3D printing parameters

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

3D printing of porous SiC ceramics added with SiO2 hollow microspheres

Preparation and properties of Si3N4 ceramics via digital light processing using Si3N4 powder coated with Al2O3-Y2O3 sintering additives

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

Mechanical and dielectric properties of porous and wave-transparent Si3N4-Si3N4 composite ceramics fabricated by 3D printing combined with chemical vapor infiltration

Preparation of high‐strength Si3N4 ceramics via vat photopolymerization: A bi‐phase particle size gradation strategy

Optimized preceramic polymer for 3D structured ceramics via fused deposition modeling

Preparation of low residual silicon content Si-SiC ceramics by binder jetting additive manufacturing and liquid silicon infiltration

Structure design influencing the mechanical performance of 3D printing porous ceramics

3D Printed Zirconia Ceramics Via Fused Deposit Modeling and Its Mechanical Properties