Abstract:3D printing is reported in the fabrication of continuous carbon fiber reinforced silicon carbide ceramic matrix composites (Cf/SiC CMCs), however, there are layer defects in the 3D printed materials, manifested as weak mechanical properties between layers. Therefore, it is essential and urgent to study how to improve the mechanical properties of 3D printed Cf/SiC CMCs at the layers. In this article, a novel processing technique which combined vertical fiber laying method with material extrusion (ME) 3D printing is proposed to manufacture Cf/SiC CMCs. A self-developed 3D printing fixed-axis rotating lifting synchronizer is adopted. The vertical fiber laying of continuous carbon fibers (Cf) in Z-direction is introduced into the X-Y printing plane. Five cycles of precursor infiltration and pyrolysis (PIP) are performed to achieve the densification of Cf/SiC CMCs. The effects of Cf bundle numbers on the flexural strength and fracture work of Cf/SiC CMCs are studied. The best performing composite is Cf/SiC CMC with six bundles, and the maximum flexural strength and fracture work is 63.84 +/- 6.62 MPa and 1291.99 +/- 161.39 J m-3, respectively. Compared with pure SiC, the fracture work of Cf/SiC CMC with 6 bundles Cf is increased by 2.54 times. This research proposes an innovative vertical fiber laying method, combined with material extrusion (ME) 3D printing technology and precursor infiltration and pyrolysis (PIP) to densification, successfully fabricating continuous carbon fiber reinforced silicon carbide ceramic matrix composites (Cf/SiC CMCs). A self-developed 3D printing fixed-axis rotating lifting synchronizer is utilized to achieve the vertical laying of Cf in Z-direction and their introduction into the X-Y printing plane.image (c) 2024 WILEY-VCH GmbH

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Additive manufacturing of complexly shaped SiC with high density via extrusion-based technique – Effects of slurry thixotropic behavior and 3D printing parameters

Additive manufacturing of high mechanical strength continuous Cf/SiC composites using a 3D extrusion technique and polycarbosilane‐coated carbon fibers

High Performance Csf/SiC Ceramic Matrix Composites Fabricated by Material Extrusion 3D Printing and Precursor Infiltration and Pyrolysis

Lattice-structured SiC ceramics obtained via 3D printing, gel casting, and gaseous silicon infiltration sintering

Preparation of low residual silicon content Si-SiC ceramics by binder jetting additive manufacturing and liquid silicon infiltration

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Application of SiO2-coated SiC Powder in Stereolithography and Sintering Densification of SiC Ceramic Composites

Fabrication of Si3N4–SiC/SiO2 composites using 3D printing and infiltration processing

Processing-microstructure correlations in material extrusion additive manufacturing for carbon fiber reinforced ceramic matrix composites

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

Fabrication of SiC Whisker-Reinforced SiC Ceramic Matrix Composites Based on 3D Printing and Chemical Vapor Infiltration Technology

Additive manufacturing of continuous carbon fiber-reinforced SiC ceramic composite with multiple fiber bundles by an extrusion-based technique

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

Thermally assisted extrusion-based 3D printing of continuous carbon fiber-reinforced SiC composites

Fabrication of complicated silicon carbide ceramic components using combined 3D printing with gelcasting

Preparation of carbon fiber-reinforced SiC ceramics by stereolithography and secondary silicon infiltration

Continuous Carbon Fiber Reinforced SiC Ceramic Matrix Composites by Vertical Fiber Laying Combined with Material Extrusion 3D Printing

Vat Photopolymerization-Based Additive Manufacturing of High-Strength RB-SiC Ceramics by Introducing Quasi-Spherical Diamond

Fabrication of High‐strength Porous SiC‐based Composites with Unidirectional Channels

SiCw/SiCp Reinforced 3D-Sic Ceramics Using Direct Ink Writing of Polycarbosilane-Based Solution: Microstructure, Composition and Mechanical Properties