Abstract:Complex silicon carbide (SiC) ceramic components are difficult to fabricate due to their strong covalent bonds. Binder jetting (BJ) additive manufacturing has the outstanding advantages of high forming efficiency and no thermal deformation, especially suitable for printing complex structure SiC components. This study tried to obtain low silicon content silicon carbide ceramics by binder jetting followed by phenolic resin impregnation and pyrolysis (PRIP) and liquid silicon infiltration (LSI). BJ was used for the SiC green parts fabrication, and the highest compressive strength (7.7 ± 0.3 MPa) and lowest dimensional deviations (1.2–1.6 mm) were obtained with the printing layer thickness of 0.15 mm. Subsequently, PRIP treatments were introduced to increase the carbon content for the following LSI process. As the number of PRIP cycles increased, the carbon density of SiC/C preform increased and the porosity decreased. After the LSI treatment, the final Si-SiC composites processed with 2 PIRP cycles reached the highest flexural strength (257 ± 14.26 MPa) and the best wear resistance. This was attributed to the low residual silicon content (10.2 vol%) and almost no residual carbon. Furthermore, several complex structural components were fabricated using these methods. The preparation of complex components verifies the feasibility of BJ and LSI for manufacturing high-strength and high-precision SiC ceramics. Besides, this work hopes to provide technical guidance for the preparation of complex SiC composites in the future.

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

Optimizing the properties of vat photopolymerization 3D-printed SiC ceramics by multi-infiltration

Additive manufacturing of Csf/SiC composites with high fiber content by direct ink writing and liquid silicon infiltration

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Preparation of low residual silicon content Si-SiC ceramics by binder jetting additive manufacturing and liquid silicon infiltration

3D-printing of polymer‐derived SiCN ceramic matrix composites by digital light processing

Enhanced Molding and Mechanical Properties of SiC-based Ceramic Lattice Structures Via Digital Light Processing

Direct Ink Writing of Chopped Carbon Fibers Reinforced Polymer-derived SiC Composites with Low shrinkage and High Strength

Optimized preceramic polymer for 3D structured ceramics via fused deposition modeling

Preparation of photosensitive SiO2/SiC ceramic slurry with high solid content for stereolithography

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Fabrication of high-strength Si/SiC composites with low shrinkage rates via vat photopolymerization technology and liquid silicon infiltration

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Additive manufacturing of continuous carbon fiber-reinforced SiC ceramic composite with multiple fiber bundles by an extrusion-based technique

Additive Manufacturing of Silicon Oxycarbide Ceramics with Minimal Surface Structures

Complex SiC-based structures with high specific strength fabricated by vat photopolymerization and one-step pyrolysis

Fabrication of dense Cf/SiC ceramic matrix composites using 3D printing and PIP with short carbon fibre as a toughening material

Additive manufacturing of high mechanical strength continuous Cf/SiC composites using a 3D extrusion technique and polycarbosilane‐coated carbon fibers

Three-dimensional printing of SiCN ceramic matrix composites from preceramic polysilazane by digital light processing

Preparation of silicon carbide ceramic slurry for stereolithography based additive manufacturing