Abstract:In this study, continuous carbon reinforced Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high entropy ceramic matrix composites were additively manufactured through paper laminating (PL), direct slurry writing (DSW), and precursor infiltration and pyrolysis (PIP). (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C high entropy ceramic (HEC) powders were synthesized by pressureless sintering and ball milling. A certain proportion of HEC powder, SiC powder, water, binder, and dispersant were mixed to prepare the HEC-SiC slurry. Meanwhile, BN coating was prepared on the 2D fiber cloth surface by the boric acid-urea method and then the cloth was cut into required shape. Additive manufacturing were conducted subsequently. Firstly, one piece of the as-treated carbon fiber cloth was auto-placed on the workbench by paper laminating (PL). Then, the HEC-SiC slurry was extruded onto the surface of the cloth by direct slurry writing (DSW). PL and DSW process were repeated, and a Cf/HEC-SiC preform was obtained after 3 cycles. At last, the preform was densified by precursor infiltration and pyrolysis (PIP) and the final Cf/HEC-SiC composite was prepared. The open porosity of the Cf/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 7.7, 10.6, and 11.3%, respectively. And the density of the Cf/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 2.9, 2.7 and 2.3 g/cm3, respectively. The mechanical properties of the Cf/HEC-SiC composites increased firstly and then decreased with the HEC content increase, reaching the maximum value when the HEC volume fraction was 30%. The mechanical properties of the Cf/HEC-SiC composites containing 45, 30 and 15% HEC were as follows: flexural strength (180.4 ± 14 MPa, 183.7 ± 4 MPa, and 173.9 ± 4 MPa), fracture toughness (11.9 ± 0.17 MPa m1/2, 14.6 ± 2.89 MPa m1/2, and 11.3 ± 1.88 MPa m1/2), and tensile strength (71.5 ± 4.9 MPa, 98.4 ± 12.2 MPa, and 73.4 ± 8.5 MPa). From this study, the additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites was achieved, opening a new insight into the manufacturing of ceramic matrix composites.

Additive manufacturing of continuous carbon fiber-reinforced SiC ceramic composite with multiple fiber bundles by an extrusion-based technique

Additive manufacturing of high mechanical strength continuous Cf/SiC composites using a 3D extrusion technique and polycarbosilane‐coated carbon fibers

Thermally assisted extrusion-based 3D printing of continuous carbon fiber-reinforced SiC composites

Additive Manufacturing of C/C-SiC Ceramic Matrix Composites by Automated Fiber Placement of Continuous Fiber Tow in Polymer with Pyrolysis and Reactive Silicon Melt Infiltration

Using flexible hydrothermal carbon-coated continuous carbon fiber to fabricate Cf/ZrB2-SiC composites by fused deposition modeling and precursor infiltration pyrolysis

Additive manufacturing of continuous carbon fiber-reinforced silicon carbide composite by fused filament fabrication and precursor infiltration pyrolysis

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Continuous carbon fiber reinforced ZrB2-SiC composites fabricated by direct ink writing combined with low-temperature hot-pressing

Slurry material extrusion of chopped carbon fiber reinforced silicon carbide ceramic matrix composites (CMCs)

Additive manufacturing of carbon fiber reinforced ceramic matrix composites based on fused filament fabrication

Additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites via paper laminating, direct slurry writing, and precursor infiltration and pyrolysis

Processing-microstructure correlations in material extrusion additive manufacturing for carbon fiber reinforced ceramic matrix composites

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Large-scale material extrusion-based additive manufacturing of short carbon fibre-reinforced silicon carbide ceramic matrix composite preforms

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Additive manufacturing of complexly shaped SiC with high density via extrusion-based technique – Effects of slurry thixotropic behavior and 3D printing parameters

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Binder jetting additive manufacturing of hierarchical structural SiC w /SiC composites

Fabrication and Formability of Continuous Carbon Fiber Reinforced Resin Matrix Composites Using Additive Manufacturing

Microstructure and mechanical property of Cf/SiC core/shell composite fabricated by direct ink writing