Abstract:In this study, continuous carbon reinforced Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high entropy ceramic matrix composites were additively manufactured through paper laminating (PL), direct slurry writing (DSW), and precursor infiltration and pyrolysis (PIP). (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C high entropy ceramic (HEC) powders were synthesized by pressureless sintering and ball milling. A certain proportion of HEC powder, SiC powder, water, binder, and dispersant were mixed to prepare the HEC-SiC slurry. Meanwhile, BN coating was prepared on the 2D fiber cloth surface by the boric acid-urea method and then the cloth was cut into required shape. Additive manufacturing were conducted subsequently. Firstly, one piece of the as-treated carbon fiber cloth was auto-placed on the workbench by paper laminating (PL). Then, the HEC-SiC slurry was extruded onto the surface of the cloth by direct slurry writing (DSW). PL and DSW process were repeated, and a Cf/HEC-SiC preform was obtained after 3 cycles. At last, the preform was densified by precursor infiltration and pyrolysis (PIP) and the final Cf/HEC-SiC composite was prepared. The open porosity of the Cf/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 7.7, 10.6, and 11.3%, respectively. And the density of the Cf/HEC-SiC composites, with the HEC volume fractions of 15, 30 and 45%, were 2.9, 2.7 and 2.3 g/cm3, respectively. The mechanical properties of the Cf/HEC-SiC composites increased firstly and then decreased with the HEC content increase, reaching the maximum value when the HEC volume fraction was 30%. The mechanical properties of the Cf/HEC-SiC composites containing 45, 30 and 15% HEC were as follows: flexural strength (180.4 ± 14 MPa, 183.7 ± 4 MPa, and 173.9 ± 4 MPa), fracture toughness (11.9 ± 0.17 MPa m1/2, 14.6 ± 2.89 MPa m1/2, and 11.3 ± 1.88 MPa m1/2), and tensile strength (71.5 ± 4.9 MPa, 98.4 ± 12.2 MPa, and 73.4 ± 8.5 MPa). From this study, the additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites was achieved, opening a new insight into the manufacturing of ceramic matrix composites.

Additive Manufacturing of C/C-SiC Ceramic Matrix Composites by Automated Fiber Placement of Continuous Fiber Tow in Polymer with Pyrolysis and Reactive Silicon Melt Infiltration

Additive manufacturing of polymer‐derived ceramic matrix composites

Fiber-laying-assisted Material Extrusion Additive Manufacturing of Continuous Carbon Fiber Reinforced SiC Ceramic Matrix Composites

Additive manufacturing of carbon fiber reinforced ceramic matrix composites based on fused filament fabrication

Additive Manufacturing of Continuous Carbon Fiber–reinforced Silicon Carbide Ceramic Composites

Additive manufacturing of high mechanical strength continuous Cf/SiC composites using a 3D extrusion technique and polycarbosilane‐coated carbon fibers

Additive manufacturing of continuous carbon fiber-reinforced SiC ceramic composite with multiple fiber bundles by an extrusion-based technique

Additive Manufacturing Cf/SiC Composites with High Fiber Content by Stereolithography Combined with Precursor Infiltration and Pyrolysis

High Performance Csf/SiC Ceramic Matrix Composites Fabricated by Material Extrusion 3D Printing and Precursor Infiltration and Pyrolysis

Processing-microstructure correlations in material extrusion additive manufacturing for carbon fiber reinforced ceramic matrix composites

Slurry material extrusion of chopped carbon fiber reinforced silicon carbide ceramic matrix composites (CMCs)

Processing and Characterization of Continuous Carbon Fiber Reinforced Silicon Oxycarbide Ceramic Matrix Composites

Additive manufacturing of continuous carbon fiber-reinforced silicon carbide composite by fused filament fabrication and precursor infiltration pyrolysis

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Rapid Fabrication of C/C-Sic Composites

Additive manufacturing of continuous carbon fiber reinforced high entropy ceramic matrix composites via paper laminating, direct slurry writing, and precursor infiltration and pyrolysis

RAPID FABRICATION OF C/SiC COMPOSITES USING CONTINUOUS SYNCHRONOUS COMPOSITE PROCESSING

Modification of the Thermoset Injection Moulding Process for Shaping to Increase the Fibre Length in C/C-SiC Ceramics Produced by the LSI Process

New Technology for Fabrication of C/Sic Composites Reinforced by Continuous Carbon Tows

High‐strength Si–SiC lattices prepared by powder bed fusion, infiltration‐pyrolysis, and reactive silicon infiltration

High Strength and High Toughness Csf/SiC Composites Prepared by Laser Powder Bed Fusion/ Reactive Melt Infiltration with the Impregnation of Boron-and Silicone-Containing Phenolic Resin