Abstract:Three-dimensional (3D) SiC/SiCf composites were fabricated by a polymer impregnation and pyrolysis (PIP) method using 3D four directional braided preforms from two kinds of SiC fibers as the reinforcements and liquid polycarbosilane as the SiC precursor.Both kinds of SiC fibers were prepared from the same precursor and process but with different heat treatment temperatures.The one prepared at a higher temperature (No.1) had a higher crystallinity than the another one (No.2).A thin pyrolytic carbon (PyC) interlayer was coated on the preforms by a methane CVD method before impregnation.Their microstructures and mechanical properties were investigated by TEM,SEM,Raman spectroscopy and mechanical tests.Results showed that both had a polycrystalline structure with grain sizes of 8-15 nm.Fiber pullout was seen from the fracture cross-section of the composites after a bending test,indicating pseudo-ductile fracture behavior.The composite using No.1 SiC fibers had an average flexural strength,elastic modulus and fracture toughness of 955.0±42.8 MPa,110.3 ± 1.7 GPa and 28.5 ±2.8 MPa· m1/2,respectively,which are Superior to those of the material formed using No.2 SiC fibers.This was ascribed to the high modulus and excellent thermal resistance of the stoichiometric No.1 SiC fibers.The PyC layer adhering to No.1 SiC fibers was ordered and smooth while that deposited on No.2 SiC fibers had a loose and granular microstructure,which was attributed to the different surface chemistries of the two types of SiC fibers.

Microstructure and mechanical property of Cf/SiC core/shell composite fabricated by direct ink writing

Microstructure Control of Highly Oriented Short Carbon Fibres in SiC Matrix Composites Fabricated by Direct Ink Writing

Fabrication and microstructure evolution of Csf/ZrB2-SiC composites via direct ink writing and reactive melt infiltration

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Microstructure and mechanical property of short fiber reinforced C/C-SiC composites

Using Pyrolytic Carbon-Coated Short Carbon Fiber to Fabricate Csf/ZrB2-SiC Composites by Direct Ink Writing and Precursor Infiltration Pyrolysis

Investigation on microstructure control of in-situ synthesized high-performance Cf/SiC composites

Fabrication of High‐strength Porous SiC‐based Composites with Unidirectional Channels

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Additive manufacturing of Csf/SiC composites with high fiber content by direct ink writing and liquid silicon infiltration

Microstructures and Mechanical Properties of Three-Dimensional Ceramic Filler Modified Carbon/carbon Composites

Microstructure, properties and mechanisms of reinforcing for C-f/SiO2 ceramic matrix composite

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles

High Performance Csf/SiC Ceramic Matrix Composites Fabricated by Material Extrusion 3D Printing and Precursor Infiltration and Pyrolysis

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Effects of In-Situ Carbon Layer and Volume Fraction of SiC Fiber on the Mechanical Properties and Fracture Behaviors of SiCf/SiC Composites Fabricated by a Modified PIP Method

Microstructure and Mechanical Property of 2.5d C/Sicn Composite

Microstructures of a carbon-fiber-reinforced silicon-carbide composite produced by precursor pyrolysis and hot pressing

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

THE MICROSTRUCTURE AND THE PROPERTY OF SiC/Si LAMINATED CERAMIC COMPOSITES FROM PAPER

Effect of Fabric Structure on Mechanical Properties and Microstructure of Cf/SiC Composites