Abstract:Previous research often failed to prepared polymer-derived SiOC ceramic components with dense and thick monoliths/skeletons based on additive manufacturing processes, due to the porosities and cracks generated during the pyrolysis process. Herein, we report a simple solution which combines the introduction of phenolic resin (PR) as an additive and the use of controlled strategy of pyrolysis, for the vat photopolymerization additively manufactured SiOC ceramics. As a result, crack-free dense monolith and lattice skeleton structural polymer-derived SiOC ceramics are successfully prepared despite the low ceramic yield of 19.3 wt% and large linear shrinkage of 50% generated after pyrolysis. The prepared dense monoliths possess a thickness of over 5 mm and the lattices show attainable maximum dense skeletons thickness of ~2 mm. The maximum dense thickness of the samples after pyrolysis is over 7 times that of other samples prepared based on additive manufacturing reported in the literature. As an indicator of dimensional retention, the specific dense thickness to ceramic yield ratio (T/Y) is deduced, resulting maximum values of 101.9 μm/(wt%) for lattice skeletons and 254.7 μm/(wt%) for monoliths. The former is even larger than that for dense monolith SiOC structures prepared by other conventional gel casting and isostatic pressing techniques with much higher ceramic yields of > 80 wt%, and is about 6.1 times the largest T/Y ratio (=16.7 μm/(wt%)) achievable in the AM-based works reported in the literature. This shows predominance of the current work over other types of polymer-derived ceramic structures prepared by additive manufacturing and even conventional methods. The lattice structures’ apparent density and specific strength reached 0.55 g/cm3 and 6.6 × 104 N∙m/kg, respectively. The mechanical performance surpasses other structural polymer-derived ceramic structures with similar apparent density reported in the literature. Through the advanced characterization and analysis of material phase and morphology evolution during the pyrolysis process, the mechanism of defect-free densification is revealed. That is, the introduction of PR enables a highly smooth gas-releasing process due to the generation of ordered gas-releasing channels in the sample bodies during the pyrolysis process. As a result, the generation of cracks and defects was successfully prevented. Moreover, due to the high carbon residue of the PR, the samples containing 15 wt% PR in the preceramic state still possessed amorphous SiOC ceramics after pyrolysis at 1400 °C, while 0 wt% PR samples showed SiC crystallization. Compared with similar materials reported, the ceramics prepared in this study exhibit enhanced structural and mechanical performance. The strategy investigated in the study can be a viable route for the additive manufacturing of high-performance crack-free and thick monolith and lattice skeleton SiOC ceramic structures based on vat photopolymerization.

Complex SiC-based structures with high specific strength fabricated by vat photopolymerization and one-step pyrolysis

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

High‐strength Si–SiC lattices prepared by powder bed fusion, infiltration‐pyrolysis, and reactive silicon infiltration

3D printing of crack-free dense polymer-derived ceramic monoliths and lattice skeletons with improved thickness and mechanical performance

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

Geometrically Complex Silicon Carbide Structures Fabricated by Robocasting

Controllable reduction of absorbance and two-step reaction for 3D-printed SiC ceramics with micron-level periodic structure

Enhanced Molding and Mechanical Properties of SiC-based Ceramic Lattice Structures Via Digital Light Processing

Vat photopolymerization 3D printing of polymer-derived SiOC ceramics with high precision and high strength

Generative shaping and material-forming (GSM) enables structure engineering of complex-shaped Li4SiO4 ceramics based on 3D printing of ceramic/polymer precursors

Optimizing the properties of vat photopolymerization 3D-printed SiC ceramics by multi-infiltration

Investigation of curing behavior and mechanical properties of SiC ceramics prepared by vat photopolymerization combined with pressureless liquid-phase sintering using Al 2 O 3 -coated SiC powder

Fabrication of high-strength Si/SiC composites with low shrinkage rates via vat photopolymerization technology and liquid silicon infiltration

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Si/SiC ceramic lattices with a triply periodic minimal surface structure prepared by laser powder bed fusion

Preparation of low residual silicon content Si-SiC ceramics by binder jetting additive manufacturing and liquid silicon infiltration

Silicon carbide ceramics manufactured by digital light processing and low temperature sintering

Silicon carbide whiskers reinforced SiOC ceramics through digital light processing 3D printing technology

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles

Additive Manufacturing of Silicon Oxycarbide Ceramics with Minimal Surface Structures

Optimized preceramic polymer for 3D structured ceramics via fused deposition modeling