Abstract:Zirconia‐toughened alumina (ZTA) ceramics with high mechanical properties were sintered by hot‐pressing method using SiC particles (SiCp) and SiC whiskers (SiCw) as the reinforcing agents simultaneously. The influences of sintering temperature, SiCp and SiCw contents on the microstructure and mechanical properties of ZTA ceramics were investigated. It was found that both SiCp and SiCw could contribute to grain refinement significantly and promote the mechanical properties of the ceramics. However, the excess addition of SiCp or SiCw led to the formation of pores with large sizes and degraded the mechanical properties instead. When 13 wt% SiCp was introduced, the maximum flexural strength of 1180.0 MPa and fracture toughness of 15.9 MPa·m1/2 were obtained, whereas the maximum flexural strength of 1314.0 MPa and fracture toughness of 14.7 MPa·m1/2 were achieved at 20 wt% SiCw. Interestingly, the simultaneous addition of SiCp and SiCw could further improve the mechanical properties, and the highest flexural strength of 1334.0 MPa and fracture toughness of 16.0 MPa·m1/2 were achieved at a SiCw/SiCp ratio of 16/4. The reinforcement mechanisms in the ceramics mainly included the phase transformation toughening of ZrO2, the crack deflection and bridging of SiCp and SiCw and the pull‐out of SiCw.

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Synergistic Toughening Effect of SiC Whiskers and Particles in ZrO2–Al2O3–SiC Ceramics

Correlation between phase content and mechanical properties of SiCw- ZTA composites sintered by SPS

Properties of ZrB2 ceramics reinforced by SiC nanowhiskers and SiC particles

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Fabrication of SiCw reinforced ZrB2-based ceramics

Preparation and Mechanical Properties of SiC Whisker and Nanosized Mullite Particulate Reinforced TZP Composites

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Mechanical properties and toughening mechanisms of SiCw/ZrO2 (6% mol Y2O3) ceramic composites

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO2–Al2O3-SiCp ceramics

Effect of SiC Whisker Content on the Properties and Microstructure of the ZrC Matrix Ultrahigh Temperature Ceramics

PREPARATION AND PROPERTIES OF SiC_(p1)/ZrB_2 ULTRA-HIGH TEMPERATURE CERAMICS

Microstructure and High-Temperature Mechanical Properties of Zro2-Al2o3-Sic Ceramics

Microstructure and Mechanical Properties of SPS Sintered Al2O3–ZrO2 (3y)–sic Ceramic Composites

Analysis of the Mechanical Properties in Short Carbon Fiber-toughened ZrB2—SiC Ultra-high Temperature Ceramic

Analysis On Toughening Mechanisms Of Different Sic Particle Reinforced Thermal Protective Ceramics

Study on Zrc-20vol.%Sicw Ultrahigh Temperature Ceramics by Hot Pressing

Microstructure and Properties of Hot Pressed Zr2(Al(Si))4C5/SiC Composites

Microstructure and mechanical properties of SiC whisker reinforced ZrO2 (2 mol% Y2O3) based composites

Microstructure and mechanical properties of ZrB2–SiC–ZrO2f ceramic

Effects of ZrB2 powders on microstructure and mechanical properties of ZrB2-SiCw ceramics