Abstract:Lithium titanate is one of the most promising candidates among advanced tritium breeders for fusion reactors. However, the tritium breeding ratio (TBR) of Li 2 TiO 3 is smaller than that of Li 2 O or Li 8 TiO 6, etc., due to its lower Li density. Therefore, new Li-containing ceramics with both high stability and high Li density need to be further explored. In this work, the Li 2+ x TiO 3 powder with high Li content was prepared by the sol-gel method, and the pebbles were fabricated by a wet forming process. The effect of excess lithium on the crystal structure and performance of Li 2+ x TiO 3 were systematically investigated. The synthesis temperature of Li 2+ x TiO 3 powder with a well-developed crystal structure prepared by this method was 500 °C, and all the diffraction patterns of sintered Li 2+ x TiO 3 ( x = 0–0.4) powder were the same as those of β-Li 2 TiO 3 phase and no second phase peaks are observed. These results demonstrated that Li 2+ x TiO 3 powder was a solid solution with high Li content. The particle size distribution of Li 2+ x TiO 3 powder was about 40–90 nm. As x = 0.3, the Li content is stable both in Li 2+ x TiO 3 powder and pebbles, and the Li 2.3 TiO 3 pebbles presented a very high relative density of 87%, a small grain size of 1.8 μm, and good sphericity of 0.98, respectively. Especially, the crushing load reached 50 N. Thus, the Li 2.3 TiO 3 solid solution pebble is an important candidate breeder material for advanced tritium breeders.Kindly check and confirm street information is correctly identified for Affiliation 1.The street information is correctly identified for Affiliation 1.We are very grateful for your additions.

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Fabrication of Li2TiO3 Pebbles by Water-Based Sol–gel Method

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Enhanced Sintering Characteristics And Microwave Dielectric Properties Of Li2tio3 Due To Nano-Size And Nonstoichiometry Effect

Synthesis of Perovskite Structure (Ca-0.61, Nd-0.26)TiO3 Nanopaticles by Sol-Gel Method

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Effect of Sintering Temperature on Microstructure and Transport Properties of Li3xLa2/3−xTiO3 with Different Lithium Contents

Low-temperature Synthesis and Characterization of Complex Perovskite (ca0.61, Nd0.26)TiO3–(Nd0.55, Li0.35)TiO3 Nanopowders and Ceramics by Sol–gel Method

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

The synthesis of nanosized TiO2 powder using a sol-gel method with TiCl4 as a precursor

Al2O3/TiO2 core/shell powder derived by novel sol–gel routes

Sol–gel Synthesis of A-site-ordered and Homogeneous (nd0.55, Li0.35)TiO3 Ceramic and Its Dielectric Properties

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Preparation and Dielectric Properties of Li2ZnTi3O8 Nanoparticles by Sol-gel Method

Preparation of Li+-Doped Tio2 Films by Sol-Gel Process

Synthesis of Ti(C,N) ultrafine powders by carbothermal reduction of TiO2 derived from sol–gel process

Solvothermal Synthesis and the Electrochemical Property of Nano-sized TiO2 Anode Materials for Lithium-ion Batteries

Effects of High Li Content on the Crystal Structure and Properties of Li2+xTiO3 Ceramic Pebbles by Sol-Gel Method