Abstract:Ni-doped TiO2 photocatalysts were prepared by low temperature combustion synthesis and some properties, such as optical absorption, crystal type, grain size distribution and chemistry transformation during temperature rising were characterized by UV-Vis DRS, X-ray diffraction (XRD), laser light dispersion grain size measurement machine and TG-DSC respectively. The photocatalytic activities of the prepared photocatalysts under visible light irradiation were evaluated by monitoring the degradation of methylene blue dye, a probe pollutant. The results indicate that the Ni-doped TiO2 photocatalysts prepared by low temperature combustion synthesis shift the optical absorption threshold to visible light, the band gap of 0.4 Ni-TiO2 (atomic ratio) is 2.3 eV, which corresponds to a 564 nm threshold in the visible light range. The crystal type of photocatalyst is anatase TiO2 and the content of NiTiO3 rise with the increase of Ni dopant. The grain size of photocatalyst distributes from 50 to 150nm, which account for 96.9% of entire quantity. During temperature rising, the TiO2 phase in photocatalyst transforms from amorphous structure to anatase and NiTiO3 crystallites appear at 445.2 degrees C. After 150 min visible light irradiation, 93.9% of methylene blue dye are degraded over 0.4 Ni-TiO2 photocatalyst. The photocatalytic activity of Ni doped TiO2 is higher than that of P25 under identical conditions.

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

The Preparation of TiO_(2-x)N_x(0<x<1) Thin Films by Sol-Gel Method and Its Photocatalysis and Hydrophilic Properties

Structure and Properties of Nitrogen-Doped Titanium Dioxide Thin Films Grown by Atmospheric Pressure Chemical Vapor Deposition

Facile low temperature immobilization of N-doped TiO2 prepared by sol–gel method

Low Temperature Hydrothermal Synthesis of N-doped TiO2 Photocatalyst with High Visible-Light Activity

Characterization and photocatalytic activity of Ni-doped tiO2 nano photocatalysts prepared by low temperature combustion synthesis]

N-doped TiO2/C nanocomposites and N-doped TiO2 synthesised at different thermal treatment temperatures with the same hydrothermal precursor.

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

Ni-doped Rutile TiO2 Nanoflowers: Low-Temperature Solution Synthesis and Enhanced Photocatalytic Efficiency

Photocatalytic Activity of Nitrogen Doped Nano-titanias and Titanium Nitride towards Methylene Blue Decolouration

Preparation and Visible Light Photocatalytic Activity of Nitrogen-doped Nano-TiO_2 Powders

Investigation of structure and properties of N-doped TiO2 thin films grown by APCVD

Preparation of TiO2 films under low temperature condition on the glass substrate

N-doped TiO2 applied in low-temperature-based dye-sensitized solar cells

Synthesis of Perovskite Structure (Ca-0.61, Nd-0.26)TiO3 Nanopaticles by Sol-Gel Method