Abstract:Nitrogen-doped TiO2 nanofibres of anatase and TiO2(B) phases were synthesised by a reaction between titanate nanofibres of a layered structure and gaseous NH3 at 400-700 °C, following a different mechanism than that for the direct nitrogen doping from TiO2. The surface of the N-doped TiO2 nanofibres can be tuned by facial calcination in air to remove the surface-bonded N species, whereas the core remains N doped. N-Doped TiO2 nanofibres, only after calcination in air, became effective photocatalysts for the decomposition of sulforhodamine B under visible-light irradiation. The surface-oxidised surface layer was proven to be very effective for organic molecule adsorption, and the activation of oxygen molecules, whereas the remaining N-doped interior of the fibres strongly absorbed visible light, resulting in the generation of electrons and holes. The N-doped nanofibres were also used as supports of gold nanoparticle (Au NP) photocatalysts for visible-light-driven hydroamination of phenylacetylene with aniline. Phenylacetylene was activated on the N-doped surface of the nanofibres and aniline on the Au NPs. The Au NPs adsorbed on N-doped TiO2(B) nanofibres exhibited much better conversion (80 % of phenylacetylene) than when adsorbed on undoped fibres (46 %) at 40 °C and 95 % of the product is the desired imine. The surface N species can prevent the adsorption of O2 that is unfavourable for the hydroamination reaction, and thus, improve the photocatalytic activity. Removal of the surface N species resulted in a sharp decrease of the photocatalytic activity. These photocatalysts are feasible for practical applications, because they can be easily dispersed into solution and separated from a liquid by filtration, sedimentation or centrifugation due to their fibril morphology.

Photocatalytic Activity of Nitrogen Doped Nano-titanias and Titanium Nitride towards Methylene Blue Decolouration

Enhanced Photocatalytic Performance of Nitrogen-Modified Titanium Dioxide

Preparation and Visible Light Photocatalytic Activity of Nitrogen-doped Nano-TiO_2 Powders

An Efficient Two-Step Technique for Nitrogen-Doped Titanium Dioxide Synthesizing: Visible-Light-Induced Photodecomposition of Methylene Blue

Preparation of Visible-Light Active N-doped Nano-Tio2 Photocatalyst by Hydrothermal Method

Photocatalytic degradation of methylene blue with nitrogen doped TiO_2 under visible light

Synthesis and Characterization of Nitrogen-Doped TiO2 Nanophotocatalyst with High Visible Light Activity

Preparation of nitrogen-doped titanium dioxide with visible-light photocatalytic activity using a facile hydrothermal method

Facile Synthesis of Nitrogen-Doped Titanium Dioxide with Enhanced Photocatalytic Properties

Preparation of Nano-Sized Nitrogen-Doped TiO2 by Mechanochemical Method and Its Photocatalytic Activity

Preparation and photocatalysis property of N-doped TiO2 film

Tuning the Surface Structure of Nitrogen-Doped TiO2 Nanofibres--an Effective Method to Enhance Photocatalytic Activities of Visible-Light-driven Green Synthesis and Degradation.

Origin Of Photocatalytic Activity Of Nitrogen-Doped Tio2 Nanobelts

Preparation and Characterization of N-doped TiO2 Nano-Powder with Visible Light Photocatalytic Activity

Photocatalytic Activity of N-doped TiO2 Photocatalysts Prepared from the Molecular Precursor (Nh4)2tio(c2o4)2

Preparation, Characterization and Visible Light Photocatalytic Activity of Nitrogen-Doped Tio2

Preparation of Visible-Light-active Carbon and Nitrogen Codoped Titanium Dioxide Photocatalysts with the Assistance of Aniline

Nitrogen-Doped Tio2 Nanotubes with Enhanced Photocatalytic Activity Synthesized by A Facile Wet Chemistry Method

Low Temperature Hydrothermal Synthesis of N-doped TiO2 Photocatalyst with High Visible-Light Activity

Interstitial N-Doped TiO2 for Photocatalytic Methylene Blue Degradation under Visible Light Irradiation