Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

The Characterization And Preparation Of Nano-Scale Fe Doping Tio2 By Sol-Gel Method - (Ii) - The Crystal Character And Grain Growth Of Fe Doping Tio2 Xerogel Powders

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Preparation and Characteristic of FexSy/TiO2 Composite Material Film

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Synthesis of Perovskite Structure (Ca-0.61, Nd-0.26)TiO3 Nanopaticles by Sol-Gel Method

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Preparation of CuO-TiO2 nanocrystalline powders by the sol-gel method

Fabrication and Optical Property Study of TiO2 Nanocrystalline Films by Sol-gel Methods

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Temperature dependence of photoluminescence, Raman scattering, and transmittance spectra of anatase Ti1-xFexO2 nanocrystalline films

Investigation of Photocatalytic and Low-Emissivity Properties of TiO 2 :F Films Featuring Columnar Structure Prepared on SnO 2 :F Substrate by Sol–gel Method

Preparation and Property of Fe~(3+)-doped TiO_2 Nanocrystal Sol

TiO2–Ag Nanocomposites by Low‐Temperature Sol–Gel Processing

Preparation of Ti Doped BaFe12O19 Ceramics by a Sol-Gel Process

Preparation of TiO2 films under low temperature condition on the glass substrate