Preparation And Characterization Of Nanosize Lanthanide Doped Mn-Zn Ferrite
XiuYing Guo,Xiuru Yan,XiaoLiang Cui,Jianping Wang,Tian Bai
DOI: https://doi.org/10.3321/j.issn:1001-4861.2004.08.006
2004-01-01
Chinese journal of inorganic chemistry
Abstract:Nanosize lanthanide doped manganese zinc ferrites were prepared by hydrothermal precipitation route using Fe-2(SO4)(3), ZnSO4.7H(2)O, MnSO4.H2O and Ln(NO3)(3) (Ln=La, Ce, Nd) as raw materials, and characterized by XRD, TEM and VSM., The results of XRD and TEM showed that lanthanide doping amount should not exceed 0.1 to maintain Mn-Zn ferrites' regular cubic spinel crystal structure and their good magnetic properties. The particles for Mn-Zn ferrites doped with different lanthanide elements were all uniformly sized nanoparticles with little aggregation and their sizes decreased in the order of La3+, Ce3+ and Nd3+. The VSM studies indicated that saturation magnetization (B.) of lanthanide doped Mn-Zn ferrite was obviously greater than that of pure Mn-Zn ferrite, and its values increased in the order of La3+, Ce3+ and Nd3+, which is consistent with their 4f electrons' numbers (4f(0), 4f(1) and 4f(3), respectively). The changing trends with lanthanide content (x) of saturation magnetization (B-S) and coercitivity (H-C) of La3+, Ce3+ and Nd3+ doped Mn-Zn ferrites were different when x was less than 0.1, which might be due to the influences of the substitution of Fe3+ on the magnetic superexchange interactions between octahedral B sites and tetrahedral A sites. On the other hand, when x was larger than 0.1, their changing trends were similar to each other.