SYNTHESIS OF NANOCRYSTALLINE Mn_(0.6)Cu_(0.2)Zn_(0.2)O(Fe_2O_3)_(0.98) FERRITE BY SOL-GEL AUTO-COMBUSTION METHOD AND CHARACTERIZATION OF ITS MAGNETIC PROPERTIES

Longtu Li

2003-01-01

Abstract:Mn 0.6 Cu 0.2 Zn 0.2 O (Fe 2O 3) 0.98 (MnCuZn) ferrite powders with particle size about 30 nm were directly synthesized by sol-gel auto_combustion method at room temperature. The thermal decomposition, nature of auto_combustion and magnetic properties of the obtained powders were investigated by DTA-TG, IR, XRD and VSM techniques. The results revealed that xerogel derived from the nitrate-citrate exhibit auto_combustion behavior once ignited in air at room temperature. The nature of auto_combustion is considered to be an oxidation_reduction process induced by heat. The results of XRD indicates that pure nanocrystalline Mn 0.6 Cu 0.2 Zn 0.2 O(Fe 2O 3) 0.98 ferrite can be directly obtained after auto_combustion without further calcination and no phase of Fe 2O 3 is detected. The phase of Fe 2O 3 would appear when the auto_combustion powders were calcined at increasing temperature. The coercive force of MnCuZn ferrite powders is linearly decreased from 9.039 5 kA·m -1 (for auto_combustion powders) to 4.724 6 kA·m -1 (for auto_combustion powders calcined at 1 000 ℃ for 2 h) while the calcined temperature increases. However, the values of saturation magnetization firstly decrease, then increase with an increase in calcined temperature. The coercive force and saturation magnetization, of obtained nanosize MnCuZn ferrite powders are high as compared to reported bulk values.