Sol gel auto combustion method to prepare nanostructures LiZnCu ferrite

Saad Shakir Hussein,Emad K. Al-Shakarchi

DOI: https://doi.org/10.1016/j.ceramint.2024.02.280

IF: 5.532

2024-02-01

Ceramics International

Abstract:A nanostructure of lithium-zinc copper ferrite (LiZnCu-Ferrite) prepared experimentally by the auto-combustion method depends on different parameters. The auto-combustion method operates at a temperature (160 °C) suitable for preparing the required nanostructure ferrite phase. The dependent composition was [Li0.5-xZnxCuxFe2.5-xO4 at (x = 0, 0.05, 0.15, 0.25, 0.35, and 0.45)]. A pre-firing at temperature (650 °C) was applied during the calcination process that was suitable to remove unwanted products. The sintering at temperature (800 °C) was suitable for a pelletized shape of ferrite samples. The X-ray diffraction (XRD) pattern showed a spinel structure of ferrite phase produced for all samples under study with the lattice constant in the range (8.345–8.368 Å) as a function of (x). The crystallite size was in the range (18.41–30.27 nm) calculated by the Scherrer method. The transmission electron microscope (TEM) showed a production of nanorods in the size range (10–45 nm) and nanoparticles in the size range (10–40 nm). There was a coincidence between the results of the XRD and TEM analyses. On the other hand, the scanning electron microscope (SEM) showed the surface morphology and the nature of grain size, which was a sign of the presence of nanostructure; it agreed with the XRD analysis. FTIR spectra showed evidence that the system Li0.5-xZnxCuxFe2.5-xO4 had spinal ferrite nanoparticles successfully prepared by sol-gel auto-combustion. A vibrating sample magnetometer (VSM) showed a change in magnetic parameters as compensation factor (x) increased for all composites of LiZnCu-ferrite such as saturation magnetization (Ms), initial magnetic permeability (μi), remanence (Mr), and coercive force (Hc) that measured from M − H loops. A saturation magnetization increased as a function of (x) and recorded a maximum value at (x = 0.15). While the coercivity, initial magnetic permeability (μi), and remanence magnetization enhanced as a function of (x) and recorded a maximum value at (x = 0.45).

materials science, ceramics