Structure phase transition and magnetic properties of nanocrystalline

JinZhi Wang,QingQing Fang

2004-01-01

Abstract:A series of nanocrystalline powders Zn0.6CoxFe2.4-xO4 ( x = 0 - 0.30) were synthesized by the sol-gel technique. The structure and magnetic properties was investigated and analyzed through the X-ray diffraction (XRD) patterns and the vibrating sample magnetometer (VSM). The experimental results show that α-Fe2O3 transitional phase appears in the temperature range from 550°C to 800°C. Single-phase zinc-cobalt ferrites with a spinel structure are obtained when the temperature is beyond 800°C. With relatively higher values of the cobalt content x = 0.075 - 0.15, the specific saturation magnetization climbs up at first and then falls down with the increase of the cobalt content. The coercive force strength Hc of Zn0.6CoxFe2.4-xO4 reaches its highest value 47520 A/ m when x=0.075 at 1300°C. Hc increases slowly with temperature near 1200°C when x≥0.15 and remains in a flat state at 1200°C - 1300°C and moderate increase is obtained by increasing the x value. High specific saturation magnetization and coercive force can be obtained simultaneously when the cobalt content is near 0.10.