Magnetism and Phase Transition for CoFe2−xMnxO4 Nanocrystalline Thin Films and Powders

B Zhou,YW Zhang,CS Liao,CH Yan

DOI: https://doi.org/10.1016/s0304-8853(02)00150-6

IF: 3.097

2002-01-01

Journal of Magnetism and Magnetic Materials

Abstract:CoFe2−xMnxO4 (x=0–2.0) nanocrystalline thin films and powders were prepared by a sol–gel process. The crystal structures and magnetic properties of the as-synthesized products were identified by an X-ray diffractometer (XRD) and an alternating gradient magnetometer (AGM), respectively. XRD analysis reveals that CoFe2−xMnxO4 nanocrystalline films and powders occurred during a cubic-to-tetragonal phase transition when x=1.5 and 1.3, respectively. The substitution of Mn3+ for Fe3+ causes the migration of Co2+ from A to B sites, and finally lead to the phase transition. AGM investigations indicate that MS, TC and HC values decrease with increasing Mn content x. The decrease of MS and TC is related to the weakly magnetic property of Mn3+; whereas, the decrease of HC is ascribed to the content decrease of Co2+ on the B sites. The large HC around the phase transformation point is induced by a structural stress originated from the metastable cubic structure.