Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

王贞,刘静,汪汝武,甘章华,徐勇攀,范丽霞,卢志红

DOI: https://doi.org/10.14136/j.cnki.issn1673-2812.2011.06.005

2011-01-01

Abstract:Amorphous Fe73.5-xCoxSi13.5B9Cu1Nb3（x=10,30,50） ribbons were prepared by the single copper wheel melt spinning technique in the air atmosphere.The nanocrystallization kinetics of amorphous ribbons was investigated by differential scanning calorimetry（DSC）.The apparent activation energies of amorphous ribbons were calculated by using Kissinger and Ozawa methods.It was found that the activation energies of the first crystallization reduce and those of the second crystallization rise with increasing Co content.The local Avrami parameter m for primary crystallization was calculated using Johnson-Mehl-Avrami（JMA） model.The values of the Avrami parameter showed that the primary crystallization mechanism of amorphous ribbons varied at different stages.In the initial stage,the crystallization mechanism was bulk crystallization with three dimensional nucleation and grain growth controlled by diffusion.In the following stage,it was surface crystallization with one dimensional nucleation and grain growth at a near zero nucleation rate.The variation of soft magnetic properties of nanocrystalline Fe63.5Co10Si13.5B9Cu1Nb3 powder cores as a function of milling time has been investigated.It was found that the effective permeability of the cores shows high frequency stability and decreases with increasing milling time.The quality factor increases with increasing frequency in the lower frequency range,reaches a maximum at the frequency of 80 kHz,and then decreases gradually with increasing frequency.