Crystallization Kinetics of Amorphous Alloys Fe73.5Si13.5-xGexB9Cu1Nb3(x=3, 6)

曾春
DOI: https://doi.org/10.11901/1005.3093.2013.603
2014-01-01
Abstract:Amorphous ribbons Fe73.5Si13.5-x Gex B9Cu1Nb3(x=3, 6) were prepared by a normal single copper wheel melt spinning technique in atmosphere, which then were isothermally annealed at 470℃、510℃、550℃ and 590℃ respectively for 1 h in a vacuum furnace. The microstructure and crystallization kinetics of the ribbons were characterized by means of X-ray diffraction(XRD), transmission electron microscopy(TEM) and differential scanning calorimeter(DSC) measurements. While the crystallization activation energies of amorphous ribbons were calculated by using Kissinger, Ozawa and Augis- Bennett models based on differential thermal analysis data. The local Avrami exponent n for primary crystallization was calculated by using Johnson-Mehl-Avrami(JMA) equation. The significant variation of local Avrami exponent n with crystallization volume fraction α demonstrated that the primary crystallization kinetics of amorphous ribbons varied at different stages. In the initial stage, the crystallization mechanism was diffusion controlled bulk crystallization with three dimensional nucleation and grain growth, while the nucleation rate deceased with time. In the following stage, it was surface crystallization with one dimensional nucleation and grain growth, while the nucleation rate was near zero. The average sizes D of α-Fe(Si,Ge) grains for the samples annealed at 510℃、550℃ and 590℃for 1 h in a vacuum furnace were less than 15 nm as confirmed both by XRD and TEM measurements.
What problem does this paper attempt to address?