Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Huan-hua ZHOU,Zhang-hua GAN,Li-ming XU,Yi DAI,Jing LIU

DOI: https://doi.org/10.3969/j.issn.1001-3830.2014.04.004

2014-01-01

Abstract:Amorphous ribbons of Fe81-xSi13BxMo2Cr1Cu1P2(x=8.6~9.6) were prepared by single-roller melt spinner in environmental atmosphere. XRD patterns of the as-spun amorphous ribbon show a small amount of crystal diffraction peaks except a wide diffuse scattering peak at low B content ofx<9.5. While the XRD patterns only show a wide diffuse scattering peak at high B range ofx≥9.5, suggesting that the ribbons should have an amorphous structure. After being optimally annealed at 520℃ for 30 min, there are mainly diffraction peaks ofα-Fe(Si) phase for each sample, while there also appears diffraction peak of FeSi phase only for the sample with B content ofx=8.6. It is found from the DTA pattern that with increasing content of B, the initial temperatureTx1 of the first crystallization peak decreases, the same as the temperature differenceΔTxbetween the first and the secondary crystallization peak. The initial magnetic permeabilityμ0 of annealed nanocrystalline alloy core increases with increasing content of B. The excellent soft magnetic properties of the studied compositions correspond to nanocrystalline alloy with B content of 9.5 % and 9.6 %.