Effect of Si/B ratio on magnetic properties and microstructure of FeSiBNbCuAl nanocrystalline alloys

Yu Sun,Jiawei Li,Lei Xie,Aina He,Yaqiang Dong,Yanxin Liu,Changjiu Wang,Kewei Zhang
DOI: https://doi.org/10.1016/j.jnoncrysol.2021.120839
2021-08-01
Abstract:<p>The effect of Si/B ratio on the magnetic properties, microstructure, magnetic domain structure, and crystallization kinetics of Fe<sub>77</sub>Si<sub>10+x</sub>B<sub>9-x</sub>Nb<sub>2</sub>Cu<sub>1</sub>Al<sub>1</sub> (x=0, 1, 2 at%) nanocrystalline alloys has been investigated. The slight increase in Si/B ratio has minimal effect on the saturation magnetization of the alloys, but effectively increases the permeability and decreases the coercivity in a wide annealing temperature range. Substituting 2% Si for B significantly increases the activation energy of α-Fe(Si) growth and Fe<sub>3</sub>B precipitation, leading to the formation of uniform, fine and stable α-Fe(Si) grains. This structure is beneficial to reduce the magnetocrystalline anisotropy and magnetoelastic anisotropy of the alloy, and form wide and smooth-moving magnetic domains, thus significantly improving the soft magnetic properties.</p>
materials science, multidisciplinary, ceramics
What problem does this paper attempt to address?
This paper aims to explore the influence of the Si/B ratio on the magnetic properties, microstructure, magnetic domain structure and crystallization kinetics of FeSiBNbCuAl nanocrystalline alloys. Specifically, the research objective is to reduce the coercivity (Hc) of the alloy and improve the annealing window by adjusting the Si/B ratio without decreasing the saturation magnetization (Bs) and permeability (μ). In the paper, Fe77Si10+xB9 - xNb2Cu1Al1 amorphous precursor ribbons with different Si/B ratios (x = 0, 1, 2 at%) were prepared, and the effects of the Si/B ratio and annealing on the crystallization behavior, microstructure and magnetic properties of these ribbons were studied. It was found that when the Si/B ratio is 12:7, the best soft magnetic properties can be obtained, and a higher Si content will make it difficult to obtain fully melt - spun amorphous ribbons. Through X - ray diffraction (XRD), transmission electron microscopy (TEM), magneto - optical Kerr microscopy and crystallization kinetics analysis, the microstructure evolution caused by the appropriate Si/B ratio for the improvement of soft magnetic properties was studied in detail.