The role of Cu content on structure and magnetic properties of Fe–Si–B–P–Cu nanocrystalline alloys

Xingjie Jia,Yanhui Li,Licheng Wu,Yan Zhang,Lei Xie,Wei Zhang

DOI: https://doi.org/10.1007/s10853-018-3131-5

IF: 4.5

2018-11-20

Journal of Materials Science

Abstract:The increase in Cu content from 1.0 to 1.7 at.% changes the as-spun Fe86-xSi2B8P4Cux and Fe84-yMn2Si2B8P4Cuy alloys from a single amorphous phase to a composite of α-Fe nanoparticles dispersing in amorphous matrix and significantly refines the nanostructure and improves the magnetic softness of the annealed alloys. The as-spun Fe82.3Mn2Si2B8P4Cu1.7 amorphous alloy containing high number density α-Fe nanoparticles forms uniform nanostructure with fine α-Fe grains in an average size of 17 nm after annealing and exhibits low coercivity of 8.4 A m−1 and high effective permeability of 15000 at 1 kHz, which are superior to those of 38 nm, 85.4 A m−1 and 1400, respectively, for the Fe83Mn2Si2B8P4Cu1 amorphous alloy. The mechanism relating to the effect of Cu content on the grain refinement was discussed in terms of the as-spun structure and crystallization process of the alloys.

materials science, multidisciplinary