Abstract:In this study, the effects of Si content on the glass-forming ability (GFA), thermal stability, annealing window, nanocrystallization process, and soft magnetic properties (SMPs) of Fe 86.3-x Si x B 10 P 2 Cu 1.7 (x = 0, 1, 2, 3, and 4, denoted as Si0, Si1, Si2, Si3, and Si4, respectively) alloys with high Fe and Cu contents were investigated. Moderate addition of Si (x = 1, 2, and 3) enhanced the GFA and suppressed the precipitation of compound phases, thus leading to a large crystallization temperature interval ( ΔT x ) exceeding 185 °C for the alloys. Appropriate addition of Si also resulted in the formation of high-density and fine pre-existing α-Fe nanocrystals in as-spun ribbons and a high growth active energy of α-Fe crystals during the subsequent nanocrystallization process for the Si1, Si2, and Si3 alloys, enhancing competitive growth between α-Fe crystals and resulting in fine nanostructure and excellent SMPs of the nanocrystalline alloys (NAs). As a result, the Si1, Si2, and Si3 NAs obtained by annealing at 420 °C for 30 min exhibited excellent SMPs with saturation magnetic flux density ( B s ) up to 1.84 T and a low coercivity ( H c ) of approximately 10 A/m. In addition, statistical analysis of the relationship between the average grain size ( D ) of α-Fe crystals and H c values of the NAs indicated that an H c α D 3 dependence is observed when the D is less than approximately 30 nm, while this dependence follows the well-known H c α D 6 relationship when the D is above 30 nm. The dependency relationship between D and H c of NAs can guide the selection of an appropriate annealing process to optimize their SMPs.

Effects of Si content on structure and soft magnetic properties of Fe81.3SixB17-xCu1.7 nanocrystalline alloys with pre-existing α-Fe nanocrystals

Effects of Si addition on crystallization process and soft magnetic properties of high-Fe and high-Cu-content Fe-Si-B-P-Cu nanocrystalline alloys

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

The role of Cu content on structure and magnetic properties of Fe–Si–B–P–Cu nanocrystalline alloys

Effects of annealing temperature and heating rate on microstructure, magnetic, and mechanical properties of high-Bs Fe81.7−xSi4B13NbxCu1.3 nanocrystalline alloys

Optimization of Crystallization Behavior and Soft Magnetic Properties of the Si-free Fe-B-P-C-Cu Nanocrystalline Alloys by Cu Content Tuning

The effect of composition on glass-forming ability, crystallization behavior, and soft magnetic properties of FeSiBCuNbNiCo amorphous/nanocrystalline alloys

Effects of Si on the microstructure, soft magnetic properties and bendability of rapidly-annealed nanocrystalline Fe–Si–B–P–Cu alloy ribbons

Effect of Ni Substitution for Si Element on Thermal and Soft Magnetic Properties of Fe73.5NixSi15.5-xB7Nb3Cu1 Nanocrystalline Alloys

Unusual alloying effects of Co and Ni on structure and magnetic properties of Fe-Si-B-Cu nanocrystalline alloys with pre-existing α-Fe nanocrystals

Local Structure, Nucleation Sites and Crystallization Behavior and Their Effects on Magnetic Properties of Fe81Si X B10P8−xCu1 (x = 0~8)

Effect of the substitution of Si for B on thermal stability, magnetic properties and corrosion resistance in novel Fe-rich amorphous soft magnetic alloy

Effect of Si/B ratio on magnetic properties and microstructure of FeSiBNbCuAl nanocrystalline alloys

Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

Effect of pre-existing nuclei on microstructure and magnetic properties of high Bs FINEMET-like nanocrystalline alloys

Excellent Soft Magnetic Properties and Enhanced Glass Forming Ability of Fe-Si-B-C-Cu Nanocrystalline Alloys

Influence of static magnetic field on rapid solidified structure and nanocrystallization behavior of Fe-Si-B-Cu soft magnetic alloys with pre-existing α-Fe nanocrystals

Effects of Mn addition on crystallization behavior and soft magnetic properties of Fe–Si–B–P–Cu nanocrystalline alloy

Effect of Si/B ratio on glass-forming ability, phase transitions and magnetic properties in (Fe40Ni40SixByCu1)0.97Nb0.03 alloys

Tailoring the thermal stability and soft magnetic properties of Fe80-Ni Si7B8P4Cu1 amorphous nanocrystalline alloys based on the magnetic domain structure

Roles of Cu in Fe-based Soft Magnetic Nanocrystalline Alloys with High Fe Content