Effects of annealing temperature and heating rate on microstructure, magnetic, and mechanical properties of high-Bs Fe81.7−xSi4B13NbxCu1.3 nanocrystalline alloys

Yanhui Li,Guozhong Zhang,Licheng Wu,Wei Zhang
DOI: https://doi.org/10.1007/s10853-020-05341-8
IF: 4.5
2020-09-29
Journal of Materials Science
Abstract:The effects of annealing temperature and heating rate on the microstructure, magnetic, and mechanical properties of melt-spun Fe81.7−xSi4B13Cu1.3Nbx (x = 0–4) alloy ribbons have been investigated. With increasing the annealing temperature, a ductile–brittle transition occurs during amorphous structure relaxation, the brittleness becomes severe with more α-Fe precipitation, and the hardness rises continuously. After annealing at respective optimum temperatures under the heating rate of 20 K/min, as the Nb content increases from 0 to 4 at.%, average grain size (Dα-Fe) and volume fraction (Vα-Fe) of the α-Fe in the nanocrystalline alloys decrease gradually from 53.3 nm and 52% to 8.7 nm and 42%, respectively; the strain at fracture (εf) representing ductile level increases from 1.33 to 1.72%; and the coercivity (Hc), saturation magnetic flux densities (Bs), and Vickers hardness (Hv) all decrease gradually. As the heating rate rises from 10 to 400 K/min, the Dα-Fe of the Fe81.7Si4B13Cu1.3 alloy decreases from 45.7 to 28.4 nm without considerable variation of the Vα-Fe; the Hc lowers from 235 to 25 A/m, the εf increases from 1.10 to 1.66%, and the Bs and Hv change slightly. Enriching of Nb weakens the dependence of nanostructure, magnetic softness, and annealing embrittlement on the heating rate. A correlation of εf ∝ Dα-Fen is found for the nanocrystalline alloys, where the n rises from − 1 to − 1/2 with enriching of Nb from 0 to 4 at.%. The mechanisms by which nanostructure affects magnetic and mechanical properties have been discussed.
materials science, multidisciplinary
What problem does this paper attempt to address?
This paper aims to study the effects of annealing temperature and heating rate on the microstructure, magnetic properties and mechanical properties of high - saturation magnetic induction intensity (Bs) Fe81.72xSi4B13NbxCu1.3 nanocrystalline alloys. Specifically: 1. **Effects of annealing temperature**: - As the annealing temperature rises, the amorphous structure relaxes, the material transforms from plasticity to brittleness, the degree of brittleness intensifies with the increase of α - Fe precipitation, and the hardness keeps rising. - At a heating rate of 20 K/min, as the Nb content increases from 0 to 4 at.%, the average grain size (Da - Fe) and volume fraction (Va - Fe) of α - Fe gradually decrease from 53.3 nm and 52% to 8.7 nm and 42% respectively; the fracture strain (ef) increases from 1.33% to 1.72%; the coercivity (Hc), saturation magnetic induction intensity (Bs) and Vickers hardness (Hv) all gradually decrease. 2. **Effects of heating rate**: - When the heating rate increases from 10 K/min to 400 K/min, the Da - Fe of Fe81.7Si4B13Cu1.3 alloy decreases from 45.7 nm to 28.4 nm, while the Va - Fe changes little; Hc decreases from 235 A/m to 25 A/m, ef increases from 1.10% to 1.66%, and Bs and Hv change slightly. - Nb - rich can weaken the heating rate dependence of nanostructure, magnetic softness and annealing brittleness. 3. **Relationship between nanostructure and properties**: - A rule related to ef/Da - Fe of nanocrystalline alloys has been found, in which the exponent n changes from - 1 to - 1/2 as the Nb content increases from 0 to 4 at.%. - The mechanism of how the nanostructure affects the magnetic and mechanical properties is discussed. Through these studies, the author hopes to better understand the relationship between nanostructure and magnetic and mechanical properties, so as to optimize the preparation process and application performance of these alloys.