Effect of annealing temperature on structure and high-temperature soft magnetic properties of (Fe0.9Co0.1)72.7Al0.8Si13.5Cu1Nb3B8V1 nanocrystalline alloy

Yan Zhang,Zhi Wang,Xian-hua Li,Qian-qian Hao,Rui-min Shi

DOI: https://doi.org/10.1016/j.materresbull.2021.111212

IF: 5.6

2021-06-01

Materials Research Bulletin

Abstract:The structure and soft magnetic properties of nanocrystalline (Fe0.9Co0.1)72.7Al0.8Si13.5Cu1Nb3B8V1 alloy annealed at 510−690 °C were investigated by XRD patterns and initial permeability. It was observed that annealing within the ranges of 510−630 °C, only soft magnetic crystalline phase precipitated from the amorphous matrix. With the increase of annealing temperature, the grain size (D) and volume fraction of the crystalline phase (Vcry ) both gradually increase from 11.9 nm to 13.7 nm and from 58 % to 89 % respectively. In the meanwhile, the thickness of the amorphous layer (Λ) gradually decreases from 2.37 nm to 0.54 nm. The change of initial permeability with temperature (μi -T curves) showed that the μi declines with increasing temperature. However, the rate of descent is different and the higher annealing temperature (Ta ) corresponds to the slower attenuation of μi . The high-temperature μi gradually improves with annealing temperature (Ta ) increasing up to 630 °C, and the higher μi of 1500 can be held up to 600 °C. However, the high-temperature μi dramatically deteriorates after annealing at 690 °C due to the precipitating hard magnetic phase from the residual amorphous matrix.

materials science, multidisciplinary