Effects of rare-earth yttrium on crystallization and magnetic properties of Fe71 .4Si13B9.6Mo2Cr1Cu1P2nanocrystalline alloy

Mingjie Dai,Liming Xu,Huanhua Zhou,Zhanghua Gan,Zhihong Lu,Jing Liu
DOI: https://doi.org/10.3969/j.issn.1674-3644.2017.02.004
2017-01-01
Abstract:Fe71.4Si13B9.6Mo2Cr1Cu1P2(y =0、0.0050、0.0077)amorphous alloy ribbons were pre-pared by a single-roller melt spinner in atmospheric environment.The effects of Y addition on the crystallization and magnetic properties of the Fe71.4Si13B9.6Mo2Cr1Cu1P2 alloy were studied by differ-ential thermal analysis,HT35 core measuring instrument and soft magnetic property measurement in-strument.The results show that with increasing content of Y,the initial crystallization temperature decreases .Compared with the sample without Y addition,the best annealing temperature decreases by about 5~10 ℃.The addition of Y can improve the maximum permeability and saturation magnetic induction intensity of the alloy.When y =0.0077,the maximum permeability of the alloy is 5.5×105 Gs/Oe and the saturation magnetic induction intensity of the alloy can reach 1.192 T.However,coer-cive force and core loss of the alloy both see a slight increase.
What problem does this paper attempt to address?