Quantitative Crystallization and Nano-Grain Size Distribution Studies of a Fecunbsib Nanocrystalline Alloy

M. S. Leu,T. S. Chin

DOI: https://doi.org/10.1557/PROC-577-557

2011-01-01

Abstract:Superior soft magnetic properties of nanocrystalline two-phase FeCuNbSiB alloy can only be attainable from a suitably nano-crystallized structure in the amorphous matrix. In this study a thermal-cycling-annealing process was adopted to anneal the amorphous specimens. The crystallization fraction of Fe 73.5 Cu 1 Nb 3 Si 13 5 B 9 ribbons after different annealing was quantitatively measured by a DTA method through the integrated crystallization enthalpy from annealed samples versus that of as-cast amorphous specimen. The crystallization fraction was estimated to be 70 % as the specimen was annealed for 550°C×7.63 ks, the optimal annealing condition. Using this method, the crystallization quantity of the crystallized FeCuNbSiB amorphous alloy was accurately estimated and controlled during nano-crystallization processes. The nanostructure of the annealed flake were investigated by high resolution TEM. The population of grain size is dominant in the range of 3-9 and 3-11 nm, corresponding to isothermal annealing at 520 and 550 °C, respectively, for 910 s. The average grain size associated with the above two annealing conditions is estimated to be 7 and 8.5 nm, respectively. The portion of nanocrystals with grain size smaller than 10 nm is about 80 % for the annealing at 520°C×910 s and 72 % for the annealing at 550°C×910 s, respectively. However, there is only one α-Fe(Si) phase evidenced in the TEM diffraction patterns.