Mechanical Alloying, Fine Structure and Thermal Decomposition of Nanocrystalline Fcc-Fe60cu40

YZ Yang,YL Zhu,QS Li,XM Ma,YD Dong,GM Wang,SQ Wei

DOI: https://doi.org/10.1016/s0921-4526(00)00531-7

2001-01-01

Abstract:The solid dissolution of Fe atoms into Cu matrix induced by mechanical alloying and subsequent thermal decomposition of Fe atoms from the solid solution in composition of Fe60Cu40 have been studied by X-ray diffraction (XRD), Mossbauer spectroscopy and the extended X-ray absorption fine structure (EXAFS) technique. The disappearance of elemental Fe and Cu XRD peaks and the presence of FCC structural XRD peaks illustrate the formation of FCC-Fe60Cu40 solid solution. Meanwhile, the new sextet spectrum with a broadening hyperfine magnetic field distribution also demonstrates that the alloying is on an atomic level and there exist complex coordination environments in the solid solution. EXAFS results Further prove the reality of atomic alloying from the clear observation of Fe atoms taking on FCC coordination in the solid solution. Additionally, a large reduction in the first shell coordination number for a center iron atom but not for a center Cu atom indicates the composition non-uniformity, which suggests that Fe atoms enrich the surface while Cu atoms enrich the core of a FCC nanocrystal. The variation of Mossbauer spectra against the annealing temperatures during thermal decomposition indicates that the Fe atoms at the surface readily nucleate and cluster into alpha -Fe at a temperature slightly below 250 degreesC, whereas the Fe atoms in the core of nano-sized crystals first cluster into gamma -Fe cohering to the FCC matrix at a temperature about 350 degreesC and then transform to alpha -Fe for further annealing at a higher temperature or for a longer time. (C) 2001 Elsevier Science B.V. All rights reserved.