Abstract:Elemental powder blends with atomic composition of Cu 100− x Ta x ( x =10, 30, 50, 70, and 90) were ball milled in a SPEX mill at several temperatures (room temperature (RT), liquid nitrogen temperature (LN 2 T), −80 °C, and 95 °C) to examine the effect of milling temperature on the extent of alloying and microstructural refinement. For the Cu-rich powders (10< x <50), high-energy ball milling to steady state at all temperatures produced a mixture of nanocrystalline Cu and Ta with no observable extension of mutual solid solubility. Compared with milling at RT, cryomilling (LN 2 T) caused further refinement of Cu crystallites, while the same steady-state grain size was reached for Ta crystallites. On the Ta-rich side (50< x <90), ball milling at all temperatures led to refined Cu and Ta grain sizes. Partial amorphization seemed to be present, which apparently increased in extent with increasing contamination from the milling media upon extended milling. Very similar results were obtained for milling at RT and LN 2 T. It was concluded that high-energy ball milling at LN 2 T did not drastically enhance the amorphization reaction between Cu and Ta nor extend their mutual solubility. The limited power of cryomilling to alloy immiscible elements such as Cu-Ta is explained as a consequence of the inability to fully suppress, during energetic collisions, the atomic mobility responsible for phase separation even when the milling is conducted at the nominal LN 2 T. The temperature dependence of milling-induced microstructural refinement and alloying is analyzed in terms of the dynamics of the generation and annihilation of the nonequilibrium vacancies in an externally driven system. It is predicted that externally forced mixing as well as diffusion assisted by high-energy ball milling can be merely weakly temperature dependent between RT and LN 2 T. As a result, the extension of solubility by using cryomilling is feasible only in limited systems, and this process cannot be expected to alloy all immiscible elements.

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

Effect of milling temperature on mechanical alloying in the immiscible Cu-Ta system

Alloying Effects on the Microstructure and Mechanical Properties of Nanocrystalline Cu-based Alloyed Thin Films: Miscible Cu-Ti Vs Immiscible Cu-Mo

SYNTHESIS OF NANOSTRUCTURED GAMMA-TiAl BASED POWDERS AND BULK ALLOYS USING HIGH ENERGY MECHANICAL MILLING AND HIP

Mechanical alloying and thermal analysis of Ta–Ti alloys

Effects of milling process parameters and PCAs on the synthesis of Al0.8Co0.5Cr1.5CuFeNi high entropy alloy powder by mechanical alloying

Low-Temperature Mechanical Alloying of Cu-Fe and Cu-Ta Powders

Effect of free energy on the solid solubility and magnetic behaviour of a mechanically alloyed nanocrystalline Cu–Co–Ti alloy

Effects of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloys

Study on mechanical alloying behavior and thermal stability of HfMoNbTaTi refractory high-entropy alloy

Investigation on microstructure and properties of Ti-45Al-5.5(Cr, Nb, B, Ta) alloy prepared by double mechanical milling (DMM) and spark plasma

Effect of temperature on mechanical behavior of Cu–Cr–Co–Ti alloys

Effect of Thermomechanical Processing on Microstructure and Mechanical Properties of CoCrFeNiMn High Entropy Alloy

Effect of Temperature on Mechanical Alloying of Cu-Zn and Cu-Cr System

Mechanical Alloying, Fine Structure and Thermal Decomposition of Nanocrystalline Fcc-Fe60cu40

Microstructure evolution of TiAl composite powder during low temperature high-energy milling

The effects of Ti and Ta on the microstructure and high temperature deformation mechanisms of the CoNi-based superalloys

Temperature Effect on Mechanical Alloying of Cu-5% Cr Powder

Alloying Effects on the Microstructure and Properties of CoCrFeMnNiX0.1 High-Entropy Alloys Via Rolling and Thermal Treatment

Synthesis and Properties of an Ultrafine Grained Ti-45al-2cr-2nb-1b-0.5ta Alloy Prepared by Double Mechanical Milling and Spark Plasma Sintering

Microstructure evolution, phase decomposition and transition of Al0.8Co0.5Cr1.5CuFeNi HEA during high temperature sintering and mechanical properties corresponding to different microstructures