Abstract:To improve the mechanical properties of Ti48Al2Cr2Nb (TiAl) alloys, Ti48Al2Cr2Nb-xTa alloy specimens without metallurgical defects were obtained by a laser additive manufacturing (LAM) technique using Ti48Al2Cr2Nb/Ta mixed powders as raw materials. The effects of different Ta contents on the microstructures, phase compositions, and tensile properties of the TiAl alloys were systematically investigated, and the relationship between these properties was established. The results showed that the lamellar structure was composed of α2 (Ti3Al), γ (TiAl), and β/B2 (β ordered to B2) phases. With the increase of Ta content, the thickness of the lamellar structure increased, and the lamellar length gradually shortened. The morphology of the α2 phase changed from an ultra-fine continuous lamellar structure to a short lamellar and an equiaxed structure. On the other hand, the morphology of the γ phase changed from lamellar to an equiaxed crystal structure, while the morphology of β/B2 phase changed from ellipsoid shape to fine block to coarse block structure. When the amount of Ta added to the TiAl powders was 0 at.%, 2 at.%, and 5 at.%, respectively, the tensile strength gradually decreased with the increase of temperature, while the elongation increased. When the amount of Ta was 8 at.%, the tensile strength at room temperature dropped to the minimum (393 MPa), and the elongation reached its maximum value (21.2%). Thus, it can be concluded that the 5 at.%Ta alloy had the best comprehensive tensile properties. The maximum tensile strength of the TiAl-5 at.%Ta alloy at room temperature, 750 °C and 850 °C, was 677 MPa, 651 MPa, and 538 MPa, respectively, and the elongation was 2.0%, 2.0%, and 13%, respectively. Compared with the TiAl-0 at.%Ta alloy, the tensile strength of TiAl-5 at.%Ta at room temperature, 750 °C, and 850 °C increased by 1.66, 2.08, and 1.9 times respectively, and the elongation increased by 1.43, 1.43, and 9.29 times, respectively.

Mechanical alloying and thermal analysis of Ta–Ti alloys

Investigation of a Hot-Pressed Nb–Ti–Al Alloy: Mechanical Alloying, Microstructure and Mechanical Property

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

Microstructural, mechanical and biological characterizations of the promising titanium-tantalum alloy for biomedical applications

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Investigation on the Microstructure and Mechanical Properties of the Ti-Ta Alloy with Unmelted Ta Particles by Laser Powder Bed Fusion

EIS Characterization of Ti Alloys in Relation to Alloying Additions of Ta

Improvement on mechanical properties and corrosion resistance of titanium-tantalum alloys in-situ fabricated via selective laser melting

Effect of Ta on Microstructures and Mechanical Properties of NiTi Alloys

Thermodynamic Assessment of Bio-Oriented Ti-Ta-Sn System

Microstructural Analysis and Mechanical Properties of TiMo20Zr7Ta15Six Alloys as Biomaterials

Exploration of Homologous Substitution Element on Phase Ratio and High Temperature Properties in High Nb-containing TiAl Alloy

Phase relationships and transformations in the ternary aluminum—titanium—tantalum system

Structure and Mechanical Properties of the New Ti30Ta20Nb Biomedical Alloy

Effect of Ta Addition on Mechanical Properties of 7715D Titanium Alloy

Effects of Tantalum on the microstructure and properties of Ti-48Al-2Cr-2Nb alloy fabricated via laser additive manufacturing

Microstructure and mechanical properties of Ta–Ti alloy by plasma-activated sintering

Cold Crucible Levitation Melting of Biomedical Ti-30 wt%Ta Alloy.

Structure and properties of titanium-aluminum alloys doped with niobium and tantalum

Effects of Tantalum on Microstructure Evolution and Mechanical Properties of High-Nb TiAl Alloys Reinforced by Ti2AlC

Microstructure of a Ti–50 Wt% Ta Alloy Produced Via Laser Powder Bed Fusion