Abstract:To improve the mechanical properties of Ti48Al2Cr2Nb (TiAl) alloys, Ti48Al2Cr2Nb-xTa alloy specimens without metallurgical defects were obtained by a laser additive manufacturing (LAM) technique using Ti48Al2Cr2Nb/Ta mixed powders as raw materials. The effects of different Ta contents on the microstructures, phase compositions, and tensile properties of the TiAl alloys were systematically investigated, and the relationship between these properties was established. The results showed that the lamellar structure was composed of α2 (Ti3Al), γ (TiAl), and β/B2 (β ordered to B2) phases. With the increase of Ta content, the thickness of the lamellar structure increased, and the lamellar length gradually shortened. The morphology of the α2 phase changed from an ultra-fine continuous lamellar structure to a short lamellar and an equiaxed structure. On the other hand, the morphology of the γ phase changed from lamellar to an equiaxed crystal structure, while the morphology of β/B2 phase changed from ellipsoid shape to fine block to coarse block structure. When the amount of Ta added to the TiAl powders was 0 at.%, 2 at.%, and 5 at.%, respectively, the tensile strength gradually decreased with the increase of temperature, while the elongation increased. When the amount of Ta was 8 at.%, the tensile strength at room temperature dropped to the minimum (393 MPa), and the elongation reached its maximum value (21.2%). Thus, it can be concluded that the 5 at.%Ta alloy had the best comprehensive tensile properties. The maximum tensile strength of the TiAl-5 at.%Ta alloy at room temperature, 750 °C and 850 °C, was 677 MPa, 651 MPa, and 538 MPa, respectively, and the elongation was 2.0%, 2.0%, and 13%, respectively. Compared with the TiAl-0 at.%Ta alloy, the tensile strength of TiAl-5 at.%Ta at room temperature, 750 °C, and 850 °C increased by 1.66, 2.08, and 1.9 times respectively, and the elongation increased by 1.43, 1.43, and 9.29 times, respectively.

Improvement on mechanical properties and corrosion resistance of titanium-tantalum alloys in-situ fabricated via selective laser melting

Selective laser melting of titanium alloy with 50 wt% tantalum: Microstructure and mechanical properties

Simultaneous improvement of strength and ductility of laser additively produced Ti6Al4V by adding tantalum

Effects of tantalum addition on microstructure and properties of titanium alloy fabricated by laser powder bed fusion

Microstructure and mechanical properties of Ta–Ti alloy by plasma-activated sintering

Effects of Tantalum on the microstructure and properties of Ti-48Al-2Cr-2Nb alloy fabricated via laser additive manufacturing

Ti-Ta-Cu Biocompatible Alloy System Development via Selective Laser Melting for Prosthetic Applications

Investigation on the Microstructure and Mechanical Properties of the Ti-Ta Alloy with Unmelted Ta Particles by Laser Powder Bed Fusion

Laser powder bed fusion of titanium-tantalum alloys: Compositions and designs for biomedical applications

Microstructural, mechanical and biological characterizations of the promising titanium-tantalum alloy for biomedical applications

Mechanical alloying and thermal analysis of Ta–Ti alloys

Research on the surface characterization, corrosion and bioactivity of nano-featured tantalum coating on selective electron beam melted Ti6Al4V alloy

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

Microstructure of a Ti–50 Wt% Ta Alloy Produced Via Laser Powder Bed Fusion

High-strength and thermally stable TiB2-modified Al–Mn–Mg–Er–Zr alloy fabricated via selective laser melting

Additive manufacturing of high-strength commercially pure titanium through lanthanum oxide addition

Mechanical, Electrochemical, and Osteoblastic Properties of Gradient Tantalum Coatings on Ti6Al4V by Prepared Plasma Alloying Technique

Microstructure, solidification behavior and mechanical properties of Al-Si-Mg-Ti/TiC fabricated by selective laser melting

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Corrosion properties of β-Ta alloyed Ti6Al4V by double-glow plasma surface alloying technique

Controlling the microstructure and mechanical properties of a metastable β titanium alloy by selective laser melting