Abstract:To improve the mechanical properties of Ti48Al2Cr2Nb (TiAl) alloys, Ti48Al2Cr2Nb-xTa alloy specimens without metallurgical defects were obtained by a laser additive manufacturing (LAM) technique using Ti48Al2Cr2Nb/Ta mixed powders as raw materials. The effects of different Ta contents on the microstructures, phase compositions, and tensile properties of the TiAl alloys were systematically investigated, and the relationship between these properties was established. The results showed that the lamellar structure was composed of α2 (Ti3Al), γ (TiAl), and β/B2 (β ordered to B2) phases. With the increase of Ta content, the thickness of the lamellar structure increased, and the lamellar length gradually shortened. The morphology of the α2 phase changed from an ultra-fine continuous lamellar structure to a short lamellar and an equiaxed structure. On the other hand, the morphology of the γ phase changed from lamellar to an equiaxed crystal structure, while the morphology of β/B2 phase changed from ellipsoid shape to fine block to coarse block structure. When the amount of Ta added to the TiAl powders was 0 at.%, 2 at.%, and 5 at.%, respectively, the tensile strength gradually decreased with the increase of temperature, while the elongation increased. When the amount of Ta was 8 at.%, the tensile strength at room temperature dropped to the minimum (393 MPa), and the elongation reached its maximum value (21.2%). Thus, it can be concluded that the 5 at.%Ta alloy had the best comprehensive tensile properties. The maximum tensile strength of the TiAl-5 at.%Ta alloy at room temperature, 750 °C and 850 °C, was 677 MPa, 651 MPa, and 538 MPa, respectively, and the elongation was 2.0%, 2.0%, and 13%, respectively. Compared with the TiAl-0 at.%Ta alloy, the tensile strength of TiAl-5 at.%Ta at room temperature, 750 °C, and 850 °C increased by 1.66, 2.08, and 1.9 times respectively, and the elongation increased by 1.43, 1.43, and 9.29 times, respectively.

Effects of tantalum addition on microstructure and properties of titanium alloy fabricated by laser powder bed fusion

Laser powder bed fusion of titanium-tantalum alloys: Compositions and designs for biomedical applications

Effects of Tantalum Concentration on the Microstructures and Mechanical Properties of Tungsten-Tantalum Alloys

Process Optimization, Interfacial Characteristics, and Mechanical Properties of Titanium-Tantalum Multi-Material Structures Fabricated Via Laser Powder Bed Fusion

Microstructure Evolution and High Strength-Ductility Synergy of Ti-13Nb-13Zr-2Ta Alloy Fabricated by Laser Powder Bed Fusion

Investigation on the Microstructure and Mechanical Properties of the Ti-Ta Alloy with Unmelted Ta Particles by Laser Powder Bed Fusion

Microstructure of a Ti–50 Wt% Ta Alloy Produced Via Laser Powder Bed Fusion

Effect of TiC on Microstructures and Mechanical Behaviors of Low-Density Nb-Ti-Al Alloys Fabricated by Laser Solid Forming

Microstructure and strengthening mechanisms of tantalum prepared using laser melting deposition

Improvement on mechanical properties and corrosion resistance of titanium-tantalum alloys in-situ fabricated via selective laser melting

Evolution of microtexture and performance in TaC/316L composites fabricated by laser powder bed fusion

Effects of Tantalum on the microstructure and properties of Ti-48Al-2Cr-2Nb alloy fabricated via laser additive manufacturing

Effects of the process parameters on the formability and properties of Ni54(at.%) Ti alloys prepared by laser powder bed fusion

Simultaneous improvement of strength and ductility of laser additively produced Ti6Al4V by adding tantalum

Advancements in Additive Manufacturing of Tantalum via the Laser Powder Bed Fusion (PBF-LB/M): A Comprehensive Review

Achieving Strength-Ductility Synergy of Laser Powder Bed Fusion Ti–6.5Al–2Zr–1Mo–1V Alloy by Regulating Laser Power

Improving the Microstructure and Mechanical Properties of Laser Powder Bed Fusion-Fabricated Tantalum by High Laser Energy Density

Optimization of Laser Powder Bed Fusion Process for Forming Porous Ta Scaffold

Fatigue Behaviour and Biocompatibility of Additively Manufactured Bioactive Tantalum Graded Lattice Structures for Load-Bearing Orthopaedic Applications.

Effect of Ta microalloying on joint performance by tailoring the microstructure during laser beam welding of Ti-22Al-27Nb

Microstructural Evolution and Mechanical Behavior of Additively Manufactured Tantalum Produced by Electron Beam Powder Bed Fusion