Abstract:Selective laser melting (SLM) is a powerful additive manufacturing (AM) technology, of which the most prominent advantage is the ability to produce components with a complex geometry. The service performances of the SLM-processed components depend on the microstructure and surface quality. In this work, the microstructures, mechanical properties, and fracture behaviors of SLM-processed Ti-6Al-4V alloy under machined and as-built surfaces after annealing treatments and hot isostatic pressing (HIP) were investigated. The microstructures were analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscopy (TEM). The mechanical properties were measured by tensile testing at room temperature. The results indicate that the as-deposited microstructures are characterized by columnar grains and fine brittle martensite and the asdeposited properties present high strength, low ductility and obvious anisotropy. After annealing at 800–900°C for 2–4 h and HIP at 920°C/100MPa for 2 h, the brittle martensite could be transformed into ductile lamellar (α+β) microstructure and the static tensile properties of SLM-processed Ti-6Al-4V alloys in the machined condition could be comparable to that of wrought materials. Even after HIP treatment, the as-built surfaces could decrease the ductility and reduction of area of SLM-processed Ti-6Al-4V alloys to 9.2% and 20%, respectively. The crack initiation could occur at the columnar grain boundaries or at the as-built surfaces. The lamellar (α+β) microstructures and columnar grains could hinder or distort the crack propagation path during tensile tests.

Selective laser melting of titanium alloy with 50 wt% tantalum: Microstructure and mechanical properties

Selective Laser Melting of Novel Titanium-Tantalum Alloy as Orthopaedic Biomaterial

Laser powder bed fusion of titanium-tantalum alloys: Compositions and designs for biomedical applications

Improvement on mechanical properties and corrosion resistance of titanium-tantalum alloys in-situ fabricated via selective laser melting

Selective laser melted near-beta titanium alloy Ti-5Al-5Mo-5V-1Cr-1Fe: Microstructure and mechanical properties

Investigation on the Microstructure and Mechanical Properties of the Ti-Ta Alloy with Unmelted Ta Particles by Laser Powder Bed Fusion

Selective laser melting of biomedical Ti15Mo alloy: A proper combination of strength and ductility under the effects of multiple mechanisms

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

Effects of tantalum addition on microstructure and properties of titanium alloy fabricated by laser powder bed fusion

Tensile Behavior of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting: Effects of Microstructures and As-Built Surface Quality

Controlling the microstructure and mechanical properties of a metastable β titanium alloy by selective laser melting

Achieving Ti-5Al-4Sn-2Zr-1Mo-0.25Si-1Nb Alloys with High Strength and Moderate Ductility through Selective Laser Melting

Microstructure of a Ti–50 Wt% Ta Alloy Produced Via Laser Powder Bed Fusion

Ti-Ta-Cu Biocompatible Alloy System Development via Selective Laser Melting for Prosthetic Applications

Simultaneous improvement of strength and ductility of laser additively produced Ti6Al4V by adding tantalum

Microstructure and strengthening mechanisms of tantalum prepared using laser melting deposition

Microstructure and Mechanical Properties of As-Built Ti-6Al-4V and Ti-6Al-7Nb Alloys Produced by Selective Laser Melting Technology

Selective Laser Melting Additive Manufactured Tantalum: Effect of Microstructure and Impurities on the Strengthening-Toughing Mechanism

Additive manufacturing of titanium alloys via selective laser melting: Fabrication, microstructure, post-processing, performance and prospect

Microstructure and mechanical properties of Ta–Ti alloy by plasma-activated sintering