Phase relationships and transformations in the ternary aluminum—titanium—tantalum system

M.L. Weaver,M.J. Kaufman

DOI: https://doi.org/10.1016/0956-7151(94)00468-w

1995-07-01

Acta Metallurgica et Materialia

Abstract:The solid-state phase transformations and phase equilibria in a series of Al-Ti-Ta alloys in the range 38–55%Al, 19–30%Ti and 20–38%Ta have been investigated. It is shown that a variety of phases exist over this composition range and that the microstructures vary dramatically with prior thermal history. For example, the disordered β phase exists at high temperatures over a large composition range and its decomposition depends strongly on both composition and cooling rate in a manner similar to that reported in titanium rich Ti-Al-Nb alloys. In addition, the α phase is shown to extend to higher Al contents than originally reported and its decomposition is similar to that observed in binary Ti-Al alloys (i.e. it forms “massive” γ at high cooling rates and α + γ or α2 + γ at slower rates). The σ-(TaxTi1−x)2Al phase becomes stable at lower temperatures in the tantalum-rich alloys studied and its formation is also shown to be a strong function of cooling rate and composition. The various results are used to suggest revisions to the ternary Al-Ti-Ta isothermal sections at both 1723 and 1623 K.