Abstract:In this study, structural, morphological, thermal and magnetic properties of amorphous-nanocrystalline Fe 70 Cr 10 Nb 10 B 10 (at.%) alloy are discussed. The formation and evaluation of amorphous-nanocrystalline structures of the alloy were followed by XRD, SEM-EDX, TEM, DTA, and VSM techniques. After 50 h of milling Cr, Nb, and B were completely dissolved into the Fe lattice forming 82% of the amorphous phase of the alloy. A gradual dissolution of the alloying elements also increased the lattice parameters concurrently. The lattice parameters reached a maximum value of 2.908 Å after 20 h of milling and then leveled off to a value of 2.891 Å at the end of 50 h of milling. Based on the XRD data, crystallite size and lattice strain of the alloy were calculated as 3.2 nm and 3.34% respectively. TEM analyses revealed that the alloy particulates comprised needle-shaped nanoparticles of an average size of 21 nm. The room temperature magnetic hysteresis loops showed that the increased duration of milling decreased the saturation magnetization from 91 to 24 emu/g. This was mainly due to the upsurge on the amorphous phase content in the alloy as the milling progressed. The increase in amorphous phase content and the subsequent reduction of the saturation magnetization were due to the inter-diffusion of the non-ferromagnetic Cr and B atoms into the Fe lattice. Thermal studies revealed that around 350 °C the amorphous phase of the alloy began crystallizing. The magnetic saturation of the heat-treated alloy also increased with the growth in the crystalline phases. The 50 h milled sample annealed at 700 °C was found to have the highest magnetic anisotropy as observed from the temperature-dependent zero-field cooled and field cooled magnetization measurements. The high-pressure X-ray diffraction measurements revealed that the amorphous state of the alloy remained stable up to 11.3 MPa. It also revealed the structural similarities of the Fe 70 Cr 10 Nb 10 B 10 alloy with those of the Fe 70 M 10 B 20 (M = Nb and Cr) types. For all practical purposes, the microstructural stability under high compressive pressure represents the consolidation properties of the nanostructured magnetic materials since both pressure and temperature-induced phase transformations are the primary controlling factors for the specific magnetization properties of the alloy.

Magnetic properties and nanocrystallization behavior of Co-based amorphous alloy

High-temperature Magnetic Properties of Fe-based Nanocrystalline Alloy

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Comprehensive study of the crystallization behavior, thermal stability, and magnetic properties of Co66.5Si15.5B12Fe4Ni2 amorphous ribbon

The Crystallization Kinetics Study of Finemet-Co Amorphous Alloys

Soft magnetic properties of Co-doped FeSiBC amorphous and nanocrystalline alloys

Evolution from Amorphous to Nanocrystalline and Corresponding Magnetic Properties of Fe-Si-B-Cu-Nb Alloys by Melt Spinning and Spark Plasma Sintering

Synthesis and characterization of amorphous-nanocrystalline Fe70Cr10Nb10B10 powders by mechanical alloying

Magnetic and structural behaviours of nanocrystalline Fe 70.8 Nb 3.7 Cu 1 Al 2.7 Mn 0.7 Si 13.5 B 7.6 alloy

Influence of Isothermal Heating on the Curie Temperature of FeCoB Bulk Amorphous Alloy

Microstructure, crystallization behavior, and soft magnetic properties of Co-doped Finemet-type nanocrystalline alloys

Magnetic Properties of Amorphous Nd2(Fe1−xCox)23

Effect of Adding Co on Crystallization Behavior and Magnetoimpedance Effect of Amorphous/Nanocrystalline FeCuNbSiB Alloy Strips

Crystallization Behavior Of An Amorphous Fe44.6co17.4cr23b15 Alloy

Influence of Nb and Mo Substitution on the Structure and Magnetic Properties of a Rapidly Quenched Fe79.4Co5Cu0.6B15 Alloy

Magnetic field annealing of FeCo-based amorphous alloys to enhance thermal stability and Curie temperature

Tailoring the thermal stability and soft magnetic properties of Fe80-Ni Si7B8P4Cu1 amorphous nanocrystalline alloys based on the magnetic domain structure

Effect of Co Substitution and Thermo-Magnetic Treatment on the Structure and Induced Magnetic Anisotropy of Fe84.5-xCoxNb5B8.5P2 Nanocrystalline Alloys

Magnetic Properties of Amorphous Nanocrystalline Alloys Based on Iron with Different Contents of Nobium in Structural Relaxation Processes