Influence of Isothermal Heating on the Curie Temperature of FeCoB Bulk Amorphous Alloy

Kinga Jez,Bartlomiej Jez,Pawel Pietrusiewicz

DOI: https://doi.org/10.37358/rc.19.9.7507

2019-10-15

Revista de Chimie

Abstract:The article presents the results of research on the thermal treatment of amorphous alloys. As part of the work, an alloy with a chemical composition Fe63Co8Y8W1B20 was produced by rapid cooling. The method used to aspirate the liquid alloy into the copper mold was used. The produced material was subjected to annealing at 940K for 10 minutes. The alloy, after solidification and after heat treatment, was subjected to structure testing by means of X-ray diffraction. The soaking process led to the partial crystallization of the amorphous precursor. Using the Faraday magnetic balance, curves of the magnetic saturation polarization as a function of temperature were recorded, on the basis of their analysis, the Curie temperature of the produced materials was determined. Using the vibration magnetometer, the primary curves of magnetization and static magnetic hysteresis loops were measured. The alloy after the soaking process was characterized by higher Curie temperature and magnetically hard properties. The test results confirm the possibility of modifying the magnetic properties of high-temperature alloys through a suitably designed heat treatment.