Abstract:The room-temperature ferromagnetism properties of Co-doped zinc oxide are reported in this paper. The Zn1-xCoxO (0.02 < x < 0.10)specimens were synthesized by the solid state reaction method with the mixture of Co2O3 and ZnO powders. The precursor Co2O3 and ZnO powders were mixed and milled for 10 h. The mixed powders were calcined at temperature of 600 degrees C and 1000 degrees C, respectively for 12 h, and then were cooled at the ambient temperature. Next, the powders were milled, made block and sintered for 12 h. The specimens were then hydrogenated at 600 degrees C for 1 h and 3 h, respectively. The room-temperature ferromagnetism (RTFM) was found in the hydrogenated samples, and the hysteresis loops of the hydrogenated Co-doped ZnO samples were measured at 10 K and 300 K by using the superconducting quantum interference device (SQUID) magnetometer (Quantum Design). The coercive field was about 310 Oe for the room-temperature measurement, and the saturation magnetization of the hydrogenated sample was about 0.056 mu(B)/Co. The samples were further measured by using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and high-resolution transmission electron microscopy (HRTEM). The results suggested the observed RTFM in the Co-doped ZnO was partly due to the existence of the cobalt nanoparticles in the hydrogenated samples. (c) 2006 Elsevier B.V. All rights reserved.

Signature Of Intrinsic High-Temperature Ferromagnetism In Cobalt-Doped Zinc Oxide Nanocrystals

Exciton quenching and ferromagnetism-to-ferrimagnetism crossover in diluted magnetic semiconducting Zn1-xCoxO nanogranular nanofibers

Variation of Structural and Magnetic Properties with Co-doping in Zn1−xCoxO Nanocrystals

High-temperature Ferromagnetism in Cobalt-Doped ZnO Single-Crystalline Nanorods

Ferromagnetism of Lightly Co-Doped Zno Nanoparticles

The Role Of Zn Interstitials In Cobalt-Doped Zno Diluted Magnetic Semiconductors

Effect of Crystallization Quality on Ferromagnetism in Zn1 − Xcoxo Nanopowders

Magnetic Anisotropy of Co2+ as Signature of Intrinsic Ferromagnetism in ZnO:Co

Structural and Magnetic Properties of Zn1-Xcoxo (0 < X <= 0.30) Nanoparticles

High-Tc ferromagnetism in a Co-doped ZnO system dominated by the formation of a zinc-blende type Co-rich ZnCoO phase.

Room-Temperature Ferromagnetism in Co-Doped Zno Fabricated by Coprecipitation Method

Coexistence of Superparamagnetism and Ferromagnetism in Co-Doped Zno Nanocrystalline Films

Hydrogenation-Induced Room-Temperature Ferromagnetism in Co-Doped ZnO Nanocrystals

Magnetic Behaviors of Co1−xZnxFe2O4 Nano-Particles

Intrinsic and Spatially Nonuniform Ferromagnetism in Co-doped ZnO Films

Room-Temperature Ferromagnetism in Co-Doped Zno Bulk Induced by Hydrogenation

Structure phase transition and magnetic properties of nanocrystalline

Ferromagnetism in manganese and cobalt co-doped ZnO bulk samples

Intrinsic magnetism of Zn1-xCoxO single-crystalline nanorods prepared by solvothermal method

H-Impurity Induced High-Temperature Ferromagnetism in Co-Doped Zno

Room-temperature Ferromagnetism in Zn_(1-x)Co_xO DMSs Prepared by Rheological Phase Reaction Method