Abstract:ZnO based diluted magnetic semiconductor particles (ZnO:Co) have been grown using a hydrothermal method with good crystallinity. The atomic percentage of Co presented in the specimen is about 0.01. Based on the x-ray diffraction and high-resolution transition electron, Co is found to be incorporated into ZnO lattice without evidence of obvious Co precipitates. However, from photoluminescence (PL) spectra in the range of 1.94 –3.45eV, a strong broad emission centered around 600nm (2.07eV) in the visible range as well as a relatively weak peak at 2.81eV are observed, indicating the presence of Co impurities. Moreover, intrinsic emissions such as DOX suggest that at least some Co have been doped into ZnO lattice, substituting for Zn2+ ions. The PL results further confirm the substitution of Zn2+ ions by Co, which leads to the changes of the electronic band structures. Magnetism could be realized at room temperature for the ZnO:Co nanoparticles under our experimental conditions although with low coercivity. The field-cooled and zero-field-cooled curves can be explained as a result of competition between the ferromagnetic and the antiferromagnetic ordering in the ZnO:Co nanoparticles. Combining the results from PL and magnetism characterization, it is reasonable to think that both doped Co in the ZnO lattice and Co impurities contribute to magnetism in ZnO:Co nanoparticles at room temperature.

Enhanced Room Temperature Ferromagnetism in Co-Doped Zno Mediated by Interstitial H

Effect of Defects on Room-Temperature Ferromagnetism in Co and Na Co-Doped ZnO

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Room-Temperature Ferromagnetism in Co-Doped Zno Bulk Induced by Hydrogenation

Room-Temperature Ferromagnetism in Co-Doped Zno Prepared by Microemulsion

Room-Temperature Ferromagnetism in Co-Doped Zno Fabricated by Coprecipitation Method

H Mediated Room Temperature Ferromagnetism in Zn0.98cu0.02o

Room-temperature Ferromagnetism in Co-doped ZnO Diluted Magnetic Semiconductor

Enhanced Room Temperature Ferromagnetism in Hydrogenated Zn0.98Mn0.02O

Hydrogenation-Induced Room-Temperature Ferromagnetism in Co-Doped ZnO Nanocrystals

Effect of thermal treatment on room-temperature ferromagnetism in Co-doped ZnO powders

Interstitial H+-Mediated Ferromagnetism in Co-Doped ZnS

Enhancement of Ferromagnetism in Zn0.98co0.02o by Quenching from High Temperatures

Synthesis of Co‐Doped ZnO Nanofibers and Their Magnetic Properties

Evidence of Oxygen Vacancy Mediated Room-Temperature-Ferromagnetism in Co-Doped Zno Films Upon Hydrogen Treatment

Room Temperature Magnetism in Co-Doped Zno Nanorods

Room-temperature Ferromagnetism in Zn_(1-x)Co_xO DMSs Prepared by Rheological Phase Reaction Method

Role of Cobalt in Room-Temperature Ferromagnetic Co-Doped Zno Thin Films

High-Temperature Ferromagnetism In (Co, Al)-Codoped Zno Powders

Enhancement of Ferromagnetic Properties in Zn0.98cu0.02o by Additional Co Doping

Defect-Bound Carrier Mediated Room-Temperature Ferromagnetism in Co-Doped ZnO Powders