Structure and Magnetic Behavior of Zn1-Xcoxo Crystal Powders Prepared by Sol-Gel Technique
Gao Qian,Sun Benzhe,Qi Yang,Qi Lianzhong
DOI: https://doi.org/10.3724/sp.j.1037.2010.00541
IF: 1.797
2011-01-01
ACTA METALLURGICA SINICA
Abstract:ZnO-based diluted magnetic semiconductors (DMSs) have been considered as one of the promising candidates for fabricating DMSs due to their initial prediction in theory of having the Curie temperature greater than room temperature, its high solubility for transition metals, and its superior semiconductor properties. Recently, Co substituted ZnO DMSs were reported frequently to show ferromagnetic properties at room temperature. However, various subsequent studies do not seem to converge on the origin of room-temperature ferromagnetism. Among the controversy, Co-cluster, Co-oxides and substitutions of Co for Zn are typical viewpoints. Meanwhile, it is not completely understood how the fabricating process influence the magnetic properties of Co-doped ZnO DMS. For this purpose, relationships among Co-doping concentration, sintered temperature, microstructure and magnetic properties of ZnO need to be invesigated particularly. In this paper, Zn1-xCoxO (x=0.01, 0.02, 0.03, 0.04 and 0.05, atomic fraction) nanocrystal powders were prepared by sol-gel technique. The crystal structure, lattice parameters; morphology and composition were characterized and analyzed by XRD, TEM, SEM and EDS, respectively. The magnetic properties were examined at room temperature using a vibrating sample magnetometer (VSM). It can be found that all the samples are composed of the particles with hexagonal wurtzite structure and the sizes of the particles are about 100 nm. For all synthesized Zn1-xCoxO samples, the lattice constants are smaller than those of un-doping ZnO crystals under the condition of the same sintered temperature. It indicates Co2+ ions have substituted Zn2+ sites. All the samples exhibit room-temperature ferromagnetic characteristics, and the ferromagnetism is their intrinsic attribute, in which the Zn0.98Co0.02O sample sintered at 500 and 700 degrees C has the highest coercivity (H-c) of 334.02 Gs and the highest remanent magnetization ratio (M-r/M-s) of 0.1813, respectively, and the Zn0.96Co0.04O sample sintered at 950 degrees C has the maximum magnetic energy product (BH) of 1.7604x10(-4) J/kg and saturation magnetization (M-s) of 0.5583 Am-2/kg. The magnetic behaviors of these samples vary not only with the concentration of Co, but also with the size of crystal grains and the concentration of oxygen vacancies. It can be found that the moderate Co content and the larger size of crystal grains are in favour of increasing room temperature ferromagnetic characteristics. Meanwhile, as far as the same concentration of Co is concerned, the smaller volume of the cell contributes to increase room temperature ferromagnetism.