Abstract:ZnO based diluted magnetic semiconductor particles (ZnO:Co) have been grown using a hydrothermal method with good crystallinity. The atomic percentage of Co presented in the specimen is about 0.01. Based on the x-ray diffraction and high-resolution transition electron, Co is found to be incorporated into ZnO lattice without evidence of obvious Co precipitates. However, from photoluminescence (PL) spectra in the range of 1.94 –3.45eV, a strong broad emission centered around 600nm (2.07eV) in the visible range as well as a relatively weak peak at 2.81eV are observed, indicating the presence of Co impurities. Moreover, intrinsic emissions such as DOX suggest that at least some Co have been doped into ZnO lattice, substituting for Zn2+ ions. The PL results further confirm the substitution of Zn2+ ions by Co, which leads to the changes of the electronic band structures. Magnetism could be realized at room temperature for the ZnO:Co nanoparticles under our experimental conditions although with low coercivity. The field-cooled and zero-field-cooled curves can be explained as a result of competition between the ferromagnetic and the antiferromagnetic ordering in the ZnO:Co nanoparticles. Combining the results from PL and magnetism characterization, it is reasonable to think that both doped Co in the ZnO lattice and Co impurities contribute to magnetism in ZnO:Co nanoparticles at room temperature.

H Mediated Room Temperature Ferromagnetism in Zn0.98cu0.02o

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Enhanced Room Temperature Ferromagnetism in Co-Doped Zno Mediated by Interstitial H

Effect of Defects on Room-Temperature Ferromagnetism in Co and Na Co-Doped ZnO

Enhanced Room Temperature Ferromagnetism in Hydrogenated Zn0.98Mn0.02O

Room Temperature Ferromagnetism in ZnO Prepared by Microemulsion

Abnormal Room Temperature Ferromagnetism in CuO/ZnO Nanocomposites Via Hydrothermal Method

Room-temperature Ferromagnetism in Co-doped ZnO Diluted Magnetic Semiconductor

Room-Temperature Ferromagnetism in Co-Doped Zno Bulk Induced by Hydrogenation

Room Temperature Multiferroicity in Zn0.98cu0.02o Film Prepared in N Plasma

Hydrogenation-Induced Room-Temperature Ferromagnetism in Co-Doped ZnO Nanocrystals

A key to room-temperature ferromagnetism in Fe-doped ZnO: Cu

Room-Temperature Ferromagnetism in Co-Doped Zno Fabricated by Coprecipitation Method

Enhancement of Ferromagnetism in Zn0.98co0.02o by Quenching from High Temperatures

Coexistence of ferromagnetism and paramagnetism in ZnO/CuO nanocomposites

Room-Temperature Ferromagnetism in Cu/Co Co-Doped ZnO Nanoparticles Prepared by the Co-Precipitation Method: For Spintronics Applications

Interstitial H+-Mediated Ferromagnetism in Co-Doped ZnS

Room Temperature Ferromagnetism in Hydrothermally Grown Ni and Cu Co-Doped ZnO Nanorods

A Cu2+ Ion–f Center Complex View on the Photoluminescence Quenching and Correlating Ferrimagnetism in (cu2+/cu12+)0.044zn0.956o Electrospun Nanobelts

Cu and Co Codoping Effects on Room-Temperature Ferromagnetism of (co,cu):Zno Dilute Magnetic Semiconductors

Substrate Effect on the Room-Temperature Ferromagnetism in Un-Doped ZnO Films