Abstract:ZnO based diluted magnetic semiconductor particles (ZnO:Co) have been grown using a hydrothermal method with good crystallinity. The atomic percentage of Co presented in the specimen is about 0.01. Based on the x-ray diffraction and high-resolution transition electron, Co is found to be incorporated into ZnO lattice without evidence of obvious Co precipitates. However, from photoluminescence (PL) spectra in the range of 1.94 –3.45eV, a strong broad emission centered around 600nm (2.07eV) in the visible range as well as a relatively weak peak at 2.81eV are observed, indicating the presence of Co impurities. Moreover, intrinsic emissions such as DOX suggest that at least some Co have been doped into ZnO lattice, substituting for Zn2+ ions. The PL results further confirm the substitution of Zn2+ ions by Co, which leads to the changes of the electronic band structures. Magnetism could be realized at room temperature for the ZnO:Co nanoparticles under our experimental conditions although with low coercivity. The field-cooled and zero-field-cooled curves can be explained as a result of competition between the ferromagnetic and the antiferromagnetic ordering in the ZnO:Co nanoparticles. Combining the results from PL and magnetism characterization, it is reasonable to think that both doped Co in the ZnO lattice and Co impurities contribute to magnetism in ZnO:Co nanoparticles at room temperature.

Room Temperature Multiferroicity in Zn 0.98 Cu 0.02 O Film Prepared in N Plasma

Room-Temperature Ferromagnetism in N-Type Cu-Doped Zno Thin Films

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Room-Temperature Ferromagnetism of Cu-Doped ZnO Films Probed by Soft X-Ray Magnetic Circular Dichroism

Room Temperature Ferromagnetic Pure Zno

Origin Of Room Temperature Ferromagnetism In Zno : Cu Films

H Mediated Room Temperature Ferromagnetism in Zn0.98cu0.02o

ROOM TEMPERATURE FERROMAGNETISM IN (N, Co)-CODOPED ZnO THIN FILMS

Room Temperature Multiferroic Behavior Of Cr-Doped Zno Films

Growth Temperature Dependent Evolutions of Microstructural, Optical and Magnetic Properties of Zn0.75Co0.25O Films

Multiferroic ZnO Obtained by Substituting Oxygen with Nitrogen

Origin Of Room Temperature Ferromagnetism In Mgo Films

Room Temperature Magnetism in Sputtered (zn,co)o Films

Role of Cobalt in Room-Temperature Ferromagnetic Co-Doped Zno Thin Films

The Intrinsic Room-Temperature Ferromagnetism in ZnO:Co Thin Films Deposited by PLD

Room Temperature Magnetic Properties of Zno Nanostructured Films

Room-Temperature Ferromagnetic Znmno Thin Films Synthesized by Plasma Enhanced Chemical Vapour Deposition Method

Room Temperature Ferromagnetism in ZnO Prepared by Microemulsion

Room-temperature Ferromagnetism in Co-doped ZnO Diluted Magnetic Semiconductor

Abnormal Room Temperature Ferromagnetism in CuO/ZnO Nanocomposites Via Hydrothermal Method

Multiferroic and Piezoelectric Behavior of Transition-Metal Doped ZnO Films