Origin Of Room Temperature Ferromagnetism In Mgo Films

jing li,yinzhu jiang,yong li,deren yang,yongbing xu,mi yan

DOI: https://doi.org/10.1063/1.4793308

IF: 4

2013-01-01

Applied Physics Letters

Abstract:We report a systematic study of the crystallinity dependence of room-temperature ferromagnetism (RTFM) in pure MgO thin films prepared by pulsed laser deposition. A sequential transition from ferromagnetism to diamagnetism as a function of deposition temperature is observed. All the samples deposited from room temperature (RT) to 200 degrees C show clear RTFM, and the magnetization decreases monotonically with the increase of the substrate temperature, whereas the MgO film grown at 300 degrees C shows diamagnetism behavior like bulk MgO sample. The maximum saturation magnetization of 8 emu/cm(3) is obtained for the MgO film deposited at RT, which degrades dramatically after crystallization under the annealing in both vacuum and air atmosphere. Further photoluminescence and X-ray photoelectron spectroscopies reveal that the ferromagnetism in the MgO thin films is correlated directly with the Mg vacancies. VC 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4793308]