Abstract:Co-doped ZnO nanorods (composition: Zn0.955Co0.045O) were grown by a simple surfactant-assisted hydrothermal technique. The morphological, structural, optical and magnetic properties of the as-prepared nanorods were investigated by means of scanning electron microscopy, high-resolution transmission electron microscopy, x-ray diffraction, x-ray photoelectron spectroscopy, micro-Raman spectroscopy, micro-cathodoluminescence, and vibrating sample magnetometry (VSM). The results showed that the sample had rod-like morphology and that the preferential growth direction was along the c axis. While Co was successfully doped into the ZnO wurtzite lattice structure as revealed by several characterization techniques, hidden secondary phases of ZnyCo3-yO4 (0 <= y <= 1) were also clearly detected by the micro-Raman spectroscopic technique. We propose that the predominant diffusion-limited Ostwald ripening crystal growth mechanism under the hydrothermal coarsening yielded such phase segregation. VSM results showed that the nanorods displayed relatively weak room-temperature ferromagnetism. We suggest that the origin of the ferromagnetism is probably due to the presence of the mixed cation valence of Co via a d-d double-exchange mechanism rather than the real doping effect. It is essential to control the crystal growth mechanism and defect states associated with the ferromagnetism in order to realize the intrinsic diluted magnetic semiconductors.

High-temperature Ferromagnetism in Cobalt-Doped ZnO Single-Crystalline Nanorods

Synthesis of 1d and Heavily Doped Zn1-Xcoxo Six-Prism Nanorods: Improvement of Blue-Green Emission and Room Temperature Ferromagnetism

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Exciton quenching and ferromagnetism-to-ferrimagnetism crossover in diluted magnetic semiconducting Zn1-xCoxO nanogranular nanofibers

Synthesis of Co‐Doped ZnO Nanofibers and Their Magnetic Properties

Synthesis And Magnetic Properties Of Zn1-Xcoxo Nanorods

Structural, Optical and Magnetic Properties of Co-Doped Zno Nanorods Prepared by Hydrothermal Method

Controllable Synthesis and Magnetic Investigation of ZnO: Co Nanowires and Nanotubes

Structural, Optical and Magnetic Properties of Co-doped ZnO Nanorods with Hidden Secondary Phases

Magnetic Property and Spatial Occupation of Co Dopants in Zn<sub>0.98</sub>Co<sub>0.02</sub>O Nanowires

Optical And Magnetic Properties Of Zn1-Xcoxo Nanorod Arrays Fabricated By Hydrothermal Method

Solution Synthesis, Optical and Magnetic Properties of Zn1−xCoxO Nanowires

Intrinsic magnetism of Zn1-xCoxO single-crystalline nanorods prepared by solvothermal method

Hydrothermal synthesis Ni-doped ZnO nanorods with room-temperature ferromagnetism

Room Temperature Ferromagnetism in Hydrothermally Grown Ni and Cu Co-Doped ZnO Nanorods

Room Temperature Magnetism in Co-Doped Zno Nanorods

Signature Of Intrinsic High-Temperature Ferromagnetism In Cobalt-Doped Zinc Oxide Nanocrystals

High-Tc ferromagnetism in a Co-doped ZnO system dominated by the formation of a zinc-blende type Co-rich ZnCoO phase.

Effect of Ferromagnetic Properties in Al-doped Zn1−xCoxO Nanowires Synthesized by Water-Assistance Reactive Vapor Deposition

Room-temperature ferromagnetic Co-doped ZnO nanoneedle array prepared by pulsed laser deposition

Synthesis and Room Temperature Ferromagnetism of Feco-Codoped Zno Nanowires